Trial manufacture of rotary friction tester and frictional force measurement of metals

In the plasma confinement type fusion reactor, in-vessel structures such as a blanket module slide at the joints each other when plasma disruption occurs, and then frictional heat is generated there. Therefore, for the selection of material and the use as the design data, it is important to understand the frictional characteristics of metals and ceramic films in the vacuum. In the present study, we have manufactured a prototype of rotary friction tester and examined the performances of the tester. The frictional characteristics of metals in the room air was measured using the friction tester, and the results obtained are as follows. A drifting friction force for a constant time and a friction force during the idling were 98 mN and 225 mN, respectively. These values were sufficiently small as compared to pressing load (9.8 - 57.8 N) used in the friction test. In a friction force measurement of stainless steel, dynamic friction force obeyed Amontons' law which indicated that dynamic friction force is not depend on either pressing load and sliding speed. The measured dynamic friction force of metals tended to decrease as the increasing hardness value of them, and it was maximum in aluminium. SEM observation of the surface for stainless steel and aluminium showed that the plastic flow was extensively generated in the mild metals during the friction test.