Influence of temperature on properties of nitrogen plasma source ion implantation (N-PSII) of Ti6A14V alloy

Specimens of Ti6Al4V alloy were implanted with nitrogen plasma source ion implantation (N-PSII) at temperatures between 100 degree C and 600 degree C to a ion dose of 4 x 10 sup 1 sup 7 cm sup - sup 2. Auger Electron Spectroscopy (AES) was used to determine the nitrogen concentration depth profiles. Microhardness measurements and pin-on-disk wear test were performed to evaluate the improvements of the surface modification. Glancing angle X-ray diffraction (XRD) was employed to determine the phases presented in the surface modified layer. The thickness of implanted layer increased by about an order of magnitude when the temperature was elevated from 100 degree C to 600 degree C. Higher surface hardness and wear resistance was also obtained at higher temperature. Scanning electron microscopy (SEM) showed distinct microstructural changes and the presence of titanium nitrides in the implanted surface