(1)H-NMR Relaxation of Ferrite Core-Shell Nanoparticles: Evaluation of the Coating Effect

We investigated the effect of different organic coatings on the (1)H-NMR relaxation properties of ultra-small iron-oxide-based magnetic nanoparticles. The first set of nanoparticles, with a magnetic core diameter [Formula: see text] = 4.4 ± 0.7 nm, was coated with polyacrylic acid (PAA) and dimercaptosuccinic acid (DMSA), while the second set, [Formula: see text] = 8.9 ± 0.9 nm, was coated with aminopropylphosphonic acid (APPA) and DMSA. At fixed core diameters but different coatings, magnetization measurements revealed a similar behavior as a function of temperature and field. On the other hand, the (1)H-NMR longitudinal [Formula: see text] nuclear relaxivity in the frequency range [Formula: see text] = 10 kHz ÷ 300 MHz displayed, for the smallest particles (diameter [Formula: see text]), an intensity and a frequency behavior dependent on the kind of coating, thus indicating different electronic spin dynamics. Conversely, no differences were found in the [Formula: see text] relaxivity of the biggest particles ([Formula: see text]) when the coating was changed. It is concluded that, when the surface to volume ratio, i.e., the surface to bulk spins ratio, increases (smallest nanoparticles), the spin dynamics change significantly, possibly due to the contribution of surface spin dynamics/topology.