Enhancing the Properties of Water-Soluble Copolymer Nanocomposites by Controlling the Layer Silicate Load and Exfoliated Nanolayers Adsorbed on Polymer Chains

Novel polymer nanocomposites of methacryloyloxy ethyl dimethyl hexadecyl ammonium bromide-modified montmorillonite (O-MMt) with acrylamide/sodium p-styrene sulfonate/methacryloyloxy ethyl dimethyl hexadecyl ammonium bromide (ASD/O-MMt) were synthesized via in situ polymerization. The molecular structures of the synthesized materials were confirmed using Fourier-transform infrared and (1)H-nuclear magnetic resonance spectroscopy. X-ray diffractometry and transmission electron microscopy revealed well-exfoliated and dispersed nanolayers in the polymer matrix, and scanning electron microscopy images revealed that the well-exfoliated nanolayers were strongly adsorbed on the polymer chains. The O-MMt intermediate load was optimized to 1.0%, and the exfoliated nanolayers with strongly adsorbed chains were controlled. The properties of the ASD/O-MMt copolymer nanocomposite, such as its resistance to high temperature, salt, and shear, were significantly enhanced compared with those obtained under other silicate loads. ASD/1.0 wt% O-MMt enhanced oil recovery by 10.5% because the presence of well-exfoliated and dispersed nanolayers improved the comprehensive properties of the nanocomposite. The large surface area, high aspect ratio, abundant active hydroxyl groups, and charge of the exfoliated O-MMt nanolayer also provided high reactivity and facilitated strong adsorption onto the polymer chains, thereby endowing the resulting nanocomposites with outstanding properties. Thus, the as-prepared polymer nanocomposites demonstrate significant potential for oil-recovery applications.