Dynamic Fracture and Crack Arrest Toughness Evaluation of High-Performance Steel Used in Highway Bridges

Impact energy tests are an efficient method of verifying adequate toughness of steel prior to it being put into service. Based on a multitude of historical correlations between impact energy and fracture toughness, minimum impact energy requirements that correspond to desired levels of fracture toug...

Descripción completa

Detalles Bibliográficos
Autores principales:	Collins, William N., Yount, Tristan D., Sherman, Ryan J., Leon, Roberto T., Connor, Robert J.
Formato:	Online Artículo Texto
Lenguaje:	English
Publicado:	MDPI 2023
Materias:	Article
Acceso en línea:	https://www.ncbi.nlm.nih.gov/pmc/articles/PMC10180142/ https://www.ncbi.nlm.nih.gov/pubmed/37176282 http://dx.doi.org/10.3390/ma16093402

Ejemplares similares

Fatigue Crack Growth Behavior and Fracture Toughness of EH36 TMCP Steel
por: Zhu, Qingyan, et al.
Publicado: (2021)

Design of highway bridges : based on AASHTO LRFD bridge design specifications /
por: Barker, R. M. (Richard M.)
Publicado: (1997)

Effects of Crack Tip Constraint on the Fracture Toughness Assessment of 9% Ni Steel for Cryogenic Application in Liquefied Natural Gas Storage Tanks
por: Kim, Young Kyun, et al.
Publicado: (2020)

Testicular Rupture: A Tough Nut to Crack
por: Holliday, Tyler L., et al.
Publicado: (2017)

Nonlinear fracture toughness measurement and crack propagation resistance of functionalized graphene multilayers
por: Cao, Changhong, et al.
Publicado: (2018)

Structural Health Monitoring of Fatigue Cracks for Steel Bridges with Wireless Large-Area Strain Sensors
por: Taher, Sdiq Anwar, et al.
Publicado: (2022)

Bouveret syndrome: a tough nut to crack
por: Ali, Ijlal Akbar, et al.
Publicado: (2019)

The hypercontractile esophagus: Still a tough nut to crack
por: Savarino, Edoardo, et al.
Publicado: (2020)

Microstructure and Pitting Corrosion of Austenite Stainless Steel after Crack Arrest
por: Zhang, Zhuwu, et al.
Publicado: (2019)

Fatigue Measurements in an Existing Highway Concrete Bridge
por: Schuler, Harald, et al.
Publicado: (2022)

Foreign body aspiration – Sometimes a tough nut to crack
por: Sandhofer, Michael J., et al.
Publicado: (2015)

Numerical Investigation of the Influence of Ultimate-Strength Heterogeneity on Crack Propagation and Fracture Toughness in Welded Joints
por: Bi, Yueqi, et al.
Publicado: (2022)

Nanoparticle-Based Tough Polymers with Crack-Propagation Resistance
por: Sasaki, Yuma, et al.
Publicado: (2023)

Rapid Thermal Processing to Enhance Steel Toughness
por: Judge, V. K., et al.
Publicado: (2018)

A Tough Case to Crack: Diagnostic, Ethical, and Legal Considerations in Treating Compulsive Neck Cracking
por: Johnson, Andrea, et al.
Publicado: (2022)

Crack-Tip Strain Field Mapping and the Toughness of Metallic Glasses
por: Hufnagel, Todd C., et al.
Publicado: (2013)

SAT-125 A Tough NUT (Midline Carcinoma) to Crack
por: Lavelle, Kristen, et al.
Publicado: (2020)

Tough and fatigue-resistant polymer networks by crack tip softening
por: Liu, Binhong, et al.
Publicado: (2023)

Effects of MgO Expansive Agent and Steel Fiber on Crack Resistance of a Bridge Deck
por: Jiang, Feifei, et al.
Publicado: (2020)

Improving Tuberculosis Vaccine Trial Efficiency: A Tough Nut to Crack
por: McShane, Helen
Publicado: (2023)

Symposium on Fracture Toughness
por: American Society for Testing and Materials. Philadelphia
Publicado: (1973)

Fracture Toughness, Breakthrough Morphology, Microstructural Analysis of the T2 Copper-45 Steel Welded Joints
por: Ding, Hao, et al.
Publicado: (2020)

Effect of H(2)S Corrosion on the Fracture Toughness of the X80 Pipeline Steel Welded Joint
por: Wang, Xueli, et al.
Publicado: (2022)

Evaluation of the Impact and Fracture Toughness of a Nanostructured Bainitic Steel with Low Retained Austenite Content
por: Brunčko, Mihael, et al.
Publicado: (2023)

Stochastic Propagation of Fatigue Cracks in Welded Joints of Steel Bridge Decks under Simulated Traffic Loading
por: Lu, Naiwei, et al.
Publicado: (2023)

Study on Fatigue Cracking of Diaphragm’s Arc Opening of OSD in Steel Bridges by Using Biaxial Stress Method
por: Zeng, Yong, et al.
Publicado: (2023)

Load Effect of Automated Truck Platooning on Highway Bridges and Loading Strategy
por: Ling, Tianyang, et al.
Publicado: (2022)

Publisher Correction: Rapid Thermal Processing to Enhance Steel Toughness
por: Judge, V. K., et al.
Publicado: (2020)

Effect of Welding Peak Temperature on Microstructure and Impact Toughness of Heat-Affected Zone of Q690 High Strength Bridge Steel
por: Zhang, Yue, et al.
Publicado: (2021)

High temperature rise dominated cracking mechanisms in ultra-ductile and tough titanium alloy
por: Choisez, L., et al.
Publicado: (2020)

The Chlamydial Type III Secretion Mechanism: Revealing Cracks in a Tough Nut
por: Betts-Hampikian, Helen Jennifer, et al.
Publicado: (2010)

Tough Nut to Crack: Transplant-acquired Food Allergy in an Adult Liver Recipient
por: Horwich, Brian H., et al.
Publicado: (2023)

A New Model for Calculation of Arrest Toughness in the Fracture Process of the Supercritical CO(2) Pipeline
por: Hu, Qihui, et al.
Publicado: (2021)

ANN and LEFM-Based Fatigue Reliability Analysis and Truck Weight Limits of Steel Bridges after Crack Detection
por: Nie, Lei, et al.
Publicado: (2022)

Uncertainty Quantification in Constitutive Models of Highway Bridge Components: Seismic Bars and Elastomeric Bearings
por: Pinto, Francisco J., et al.
Publicado: (2023)

An ultrafast time-resolution method based on picosecond pulsed laser for determining rock fracture toughness at multipoint during the crack propagation
por: Zhang, Mingyuan, et al.
Publicado: (2022)

The Highways
Publicado: (1893)

Highways
por: Benedict, A. L.
Publicado: (1917)

Impact Fracture Surfaces as the Indicators of Structural Steel Post-Fire Susceptibility to Brittle Cracking
por: Maslak, Mariusz, et al.
Publicado: (2023)

Symposium on Fatigue and Fracture Toughness
por: American Society for Testing and Materials. Philadelphia
Publicado: (1974)

Cannot write session to /tmp/vufind_sessions/sess_mg1sm2jh1nu8tqmig8iuh9p3n9