Novel polymer composite coated with ethylcellulose nanoparticle from waste paper as an alternative material to extracorporeal oxygenation membrane

Extracorporeal membrane oxygenator (ECMO) is a valuable technology to support people with acute respiratory distress syndrome (ARDS) and is recommended for COVID-19 patients. This study aims to fabricate polymer-based composite membranes coated with ethylcellulose nanoparticles from waste paper and identify the performance of the composite as ECMO candidates. Composite membranes were made from four types of polymers, namely, nylon, PTFE (polytetrafluoroethylene), Pebax(®) MH-1657, and SBS (poly-(styrene-b-butadiene-b-styrene)). PDMS (polydimethylsiloxane) 1 wt.% and ethylcellulose nanoparticles (3% and 10 wt.%) were used as membrane coatings to increase their hydrophobic properties. The success of cellulose isolation and ethylcellulose synthesis from waste paper was confirmed by the FTIR and XRD analysis. The size of the synthesized ethylcellulose nanoparticles was 32.68 nm. The coating effect on composite membranes was studied by measuring the contact angle, membrane porosity, protein quantification tests, and single gas permeation of O(2) and CO(2). Based on the protein quantification test, the protein could not pass through the Pebax/PDMS and SBS/PDMS composites coated with 10 wt.% ethylcellulose; this indicated less risk of plasma leakage. The gas permeation test on nylon/PDMS, PTFE/PDMS, and SBS/PDMS composites coated with 10% ethylcellulose resulted high CO(2)/O(2) selectivity, respectively, 2.17, 3.48, and 3.22 as good indication for extracorporeal oxygenation membrane. SUPPLEMENTARY INFORMATION: The online version contains supplementary material available at 10.1007/s10965-023-03576-y.