Ternary Metal (Cu–Ni–Zn) Oxide Nanocomposite via an Environmentally Friendly Route

[Image: see text] In this work, we report the engineering of sub-30 nm nanocomposites of CuO/ZnO/NiO by using Dodonaea viscosa leaf extract. Zinc sulfate, nickel chloride, and copper sulfate were used as salt precursors, and isopropyl alcohol and water were used as solvents. The growth of nanocomposites was investigated by varying the concentrations of precursors and surfactants at pH 12. The as-prepared composites were characterized by XRD analysis and found to have CuO (monoclinic), ZnO (hexagonal primitive), and NiO (cubic) phases with an average size of 29 nm. FTIR analysis was performed to investigate the mode of fundamental bonding vibrations of the as-prepared nanocomposites. The vibrations of the prepared CuO/ZnO/NiO nanocomposite were detected at 760 and 628 cm(–1), respectively. The optical bandgap energy of the CuO/NiO/ZnO nanocomposite was 3.08 eV. Ultraviolet–visible spectroscopy was performed to calculate the band gap by the Tauc approach. Antimicrobial and antioxidant activities of the synthesized CuO/NiO/ZnO nanocomposite were investigated. It was found that the antimicrobial activity of the synthesized nanocomposite increases with an increase in the concentration. The antioxidant activity of the synthesized nanocomposite was examined by using both ABTS and DPPH assays. The obtained results show an IC(50) value of 0.110 for the synthesized nanocomposite compared to DPPH and ABTS (0.512), which is smaller than that of ascorbic acid (IC(50) = 1.047). Such a low IC(50) value ensures that the antioxidant potential of the nanocomposite is higher than that of ascorbic acid, which in turn shows their excellent antioxidant activity against both DPPH and ABTS.