Abrasive Wear Resistance of Ultrafine Ausferritic Ductile Iron Intended for the Manufacture of Gears for Mining Machinery
The purpose of this study was to experimentally determine the abrasion wear properties of ausferritic ductile iron austempered at 250 °C in order to obtain cast iron of class EN-GJS-1400-1. It has been found that such a cast iron grade makes it possible to create structures for material conveyors us...
Autores principales: | , , , , , , , |
---|---|
Formato: | Online Artículo Texto |
Lenguaje: | English |
Publicado: |
MDPI
2023
|
Materias: | |
Acceso en línea: | https://www.ncbi.nlm.nih.gov/pmc/articles/PMC10305286/ https://www.ncbi.nlm.nih.gov/pubmed/37374495 http://dx.doi.org/10.3390/ma16124311 |
Sumario: | The purpose of this study was to experimentally determine the abrasion wear properties of ausferritic ductile iron austempered at 250 °C in order to obtain cast iron of class EN-GJS-1400-1. It has been found that such a cast iron grade makes it possible to create structures for material conveyors used for short-distance transport purposes, required to perform in terms of abrasion resistance under extreme conditions. The wear tests addressed in the paper were conducted at a ring-on-ring type of test rig. The test samples were examined under the conditions of slide mating, where the main destructive process was surface microcutting via loose corundum grains. The mass loss of the examined samples was measured as a parameter characteristic of the wear. The volume loss values thus obtained were plotted as a function of initial hardness. Based on these results, it has been found that prolonged heat treatment (of more than 6 h) causes only an insignificant increase in the resistance to abrasive wear. |
---|