Effectiveness of Two Intensity Levels of Diode Laser in Debonding Metallic Brackets Regarding Enamel Surface Integrity and Pulpal Temperature: An Ex-Vivo Study

Introduction: The traditional methods of deboning metal brackets exert excessive force, resulting in enamel scratches, fractures, and patient discomfort. The objective of this study was to evaluate the effectiveness of using two intensity levels of a diode laser for debonding metallic orthodontic brackets as an alternative to the conventional debonding method. Materials and methods: Sixty intact, extracted human premolar teeth were used in this study, and metal orthodontic brackets were bonded to the buccal surface of these teeth. The teeth were divided into three groups for the experiment: (1) the control group, where conventional bracket debonding was performed using a debonding plier, (2) the first experimental group, where a diode laser (2.5W, 980nm) was utilized for laser debonding, and (3) the second experimental group, where a diode laser (5W, 980nm) was used for laser debonding. The laser was applied using a sweeping movement for 5 seconds. After debonding, the adhesive remnant index (ARI), the lengths, and the frequency of enamel cracks were compared among the groups. Additionally, an increase in intra-pulpal temperature was measured. Results: In all groups, there were no instances of enamel fractures. Laser debonding resulted in a significant reduction in both the frequency and length of newly formed enamel cracks compared to the conventional debonding method. The laser debonding group exhibited increases in intra-pulpal temperature of 2.37°C and 3.60°C in the second and third groups, respectively. These temperature increases were significantly lower than the threshold of 5.5°C. There were no significant differences observed in the ARI scores among the groups. Conclusion: With all debonding methods, an increase in the length and frequency of enamel cracks should be anticipated. However, laser-assisted debonding of metal brackets offers the advantage of reducing the risk of enamel damage while avoiding thermal damage to the pulp.