Crack Size and Undermatching Effects on Fracture Behavior of a Welded Joint

Crack size and undermatching effects on fracture behavior of undermatched welded joints are presented and analyzed. Experimental and numerical analysis of the fracture behavior of high-strength low-alloyed (HSLA) steel welded joints with so-called small and large crack in undermatched weld metal and...

Descripción completa

Detalles Bibliográficos
Autores principales:	Sedmak, Aleksandar, Doncheva, Elisaveta, Medjo, Bojan, Rakin, Marko, Milosevic, Nenad, Radu, Dorin
Formato:	Online Artículo Texto
Lenguaje:	English
Publicado:	MDPI 2023
Materias:	Article
Acceso en línea:	https://www.ncbi.nlm.nih.gov/pmc/articles/PMC10343383/ https://www.ncbi.nlm.nih.gov/pubmed/37445171 http://dx.doi.org/10.3390/ma16134858

Ejemplares similares

Determination of the Actual Stress–Strain Diagram for Undermatching Welded Joint Using DIC and FEM
por: Milošević, Nenad Zoran, et al.
Publicado: (2021)

Numerical and Experimental Investigations of Fracture Behaviour of Welded Joints with Multiple Defects
por: Aranđelović, Mihajlo, et al.
Publicado: (2021)

Effect of Shielding Gas Arc Welding Process on Cavitation Resistance of Welded Joints of AlMg4.5Mn Alloy
por: Dojčinović, Marina, et al.
Publicado: (2023)

The Effect of Material Heterogeneity and Temperature on Impact Toughness and Fracture Resistance of SA-387 Gr. 91 Welded Joints
por: Jovanović, Milivoje, et al.
Publicado: (2022)

Tensile Strain Capacity Prediction Model of an X80 Pipeline with Improper Transitioning and Undermatched Girth Weld
por: Chen, Hongyuan, et al.
Publicado: (2022)

Effect of Temperature on S32750 Duplex Steel Welded Joint Impact Toughness
por: Perković, Srđa, et al.
Publicado: (2023)

Low-Cycle Fatigue Behavior of 10CrNi3MoV High Strength Steel and Its Undermatched Welds
por: Song, Wei, et al.
Publicado: (2018)

Numerical Investigation of the Influence of Ultimate-Strength Heterogeneity on Crack Propagation and Fracture Toughness in Welded Joints
por: Bi, Yueqi, et al.
Publicado: (2022)

Upper Bound Limit Load Solutions for Welded Joints with Cracks
por: Alexandrov, Sergey
Publicado: (2012)

Effect of Yield Strength Distribution Welded Joint on Crack Propagation Path and Crack Mechanical Tip Field
por: Bi, Yueqi, et al.
Publicado: (2021)

Showing high-achieving college applicants past admissions outcomes increases undermatching
por: Tomkins, Sabina, et al.
Publicado: (2023)

Microstructure, Mechanical Properties and Fatigue Crack Growth Behavior of Gas Tungsten Arc Welding Welded Joint of the Hastelloy N Alloy
por: Wang, Sai, et al.
Publicado: (2023)

Analysis of Crack Propagation Behaviors in RPV Dissimilar Metal Welded Joints Affected by Residual Stress
por: Zhao, Lingyan, et al.
Publicado: (2023)

Weld Magnification Factor Approach in Cruciform Joints Considering Post Welding Cooling Medium and Weld Size
por: Araque, Oscar, et al.
Publicado: (2018)

Computational modeling of fatigue crack propagation in butt welded joints subjected to axial load
por: Araque, Oscar, et al.
Publicado: (2019)

Hot-Cracking Mechanism of Laser Welding of Aluminum Alloy 6061 in Lap Joint Configuration
por: Rakhi, Km, et al.
Publicado: (2023)

Fatigue Crack Growth Behavior of the MIG Welded Joint of 06Cr19Ni10 Stainless Steel
por: Tang, Lanqing, et al.
Publicado: (2018)

Low-Income Students in Higher Education: Undermatching Predicts Decreased Satisfaction toward the Final Stage in College
por: Muskens, Marjolein, et al.
Publicado: (2019)

A New Microstructural Approach to the Strength of an Explosion Weld
por: Kolpakov, Alexander G., et al.
Publicado: (2022)

Uncertainty Modeling of Fatigue Crack Growth and Probabilistic Life Prediction for Welded Joints of Nuclear Stainless Steel
por: Chang, Haijun, et al.
Publicado: (2020)

Effect of Mechanical Heterogeneity on Strain and Stress Fields at Crack Tips of SCC in Dissimilar Metal Welded Joints
por: Zhang, Shun, et al.
Publicado: (2021)

Stochastic Propagation of Fatigue Cracks in Welded Joints of Steel Bridge Decks under Simulated Traffic Loading
por: Lu, Naiwei, et al.
Publicado: (2023)

Inhibiting weld cracking in high-strength aluminium alloys
por: Hu, Yanan, et al.
Publicado: (2022)

Influence of Welding Speed on Fracture Toughness of Friction Stir Welded AA2024-T351 Joints
por: Milčić, Miodrag, et al.
Publicado: (2021)

Yield Load Solutions for SE(B) Fracture Toughness Specimen with I-Shaped Heterogeneous Weld
por: Konjatić, Pejo, et al.
Publicado: (2021)

Development of Coated Electrodes with Solid Wire and Flux-Cored Alloyed Wire for Microalloyed Steel Welding
por: Bajić, Darko, et al.
Publicado: (2020)

Experimental and Numerical Analysis of Fracture Mechanics Behavior of Heterogeneous Zones in S690QL1 Grade High Strength Steel (HSS) Welded Joint
por: Tomerlin, Damir, et al.
Publicado: (2023)

Improved Formula for the Stress Intensity Factor of Semi-Elliptical Surface Cracks in Welded Joints under Bending Stress
por: Peng, Yang, et al.
Publicado: (2017)

Effect of Material Heterogeneity on Environmentally Assisted Cracking Growth Rate of Alloy 600 for Safe-End Welded Joints
por: Zhao, Kuan, et al.
Publicado: (2021)

Fatigue Property and Small Crack Propagation Mechanism of MIG Welding Joint of 6005A-T6 Aluminum Alloy
por: Peng, Zeng, et al.
Publicado: (2022)

Relaxation behavior of polyethylene welded joints
por: Demchenko, Valeriy, et al.
Publicado: (2017)

Initiation and growth kinetics of solidification cracking during welding of steel
por: Aucott, L., et al.
Publicado: (2017)

Repair of a Cracked Historic Maryan Bell by Gas Welding
por: Bartocha, Dariusz, et al.
Publicado: (2021)

Welded joint design
por: Hicks, J. G. (John G.)
Publicado: (1999)

Effect of Post-Weld Heat Treatment on Microstructure and Fracture Toughness of X80 Pipeline Steel Welded Joint
por: Wang, Xueli, et al.
Publicado: (2022)

Determining the Role of Acicular Ferrite Carbides in Cleavage Fracture Crack Initiation for Two Medium Carbon Microalloyed Steels
por: Jovanović, Gvozden, et al.
Publicado: (2023)

Lamb Wave Line Sensing for Crack Detection in a Welded Stiffener
por: An, Yun-Kyu, et al.
Publicado: (2014)

Modeling the Crack Interference in X80 Oil and Gas Pipeline Weld
por: Cui, Wei, et al.
Publicado: (2023)

A Brief Overview on Crack Patterns, Repair and Strengthening of Historical Masonry Structures
por: Latifi, Reza, et al.
Publicado: (2023)

Experimental and Numerical Investigation of the Fracture Behavior of Welded Aluminum Cross Joints under Axial Compression
por: Panwitt, Hannes, et al.
Publicado: (2020)

Cannot write session to /tmp/vufind_sessions/sess_e7rnlgrf58noe4qo0gg8v48lrs