Fire resistance of low alloy Q420d high-strength steel column under high-temperature creep

The high-temperature mechanical and creep characteristics of Q420D steel are investigated in this essay. To determine the steel's high-temperature yield strength, the high-temperature tensile test of Q420D steel was first performed. In the temperature range of 400°C–800°C, the high-temperature creep test under various pressures was conducted, and the creep strain curve over time was produced. Finite element analysis and comparison were done to examine the impact of creep strain on the Q420D steel column's bearing capacity under high-temperature conditions. The findings demonstrated that: Using Abaqus, a finite element fire resistance analysis of a Q420D steel column, was conducted while taking initial geometrical flaws, residual stress, and creep effect into account. As a result, the critical temperature of a Q420D steel column under various load ratios was determined. The largest deviation from the critical temperature in the standard GB51249–2017 was 2.9% when the creep effect was taken into account under the load ratio R = 0.3. The highest reduction in fire resistance limit time under low load ratio conditions, taking into account the creeping impact of Q420D steel columns, is 35%. The findings demonstrate that the high-temperature creep energy greatly lowers the steel column's fire resistance.