A Novel UV Barrier Poly(lactic acid)/Poly(butylene succinate) Composite Biodegradable Film Enhanced by Cellulose Extracted from Coconut Shell

Cellulose was extracted from coconut shell powder (CSP) as a renewable biomass resource and utilized as a reinforcing material in poly(lactic acid)/poly(butylene succinate) (PLA/PBS) solvent casting films. The extraction process involved delignification and mercerization of CSP. Microscopic investig...

Descripción completa

Detalles Bibliográficos
Autores principales: He, Xiaoyan, Tang, Lisheng, Zheng, Jun, Jin, Yuanyuan, Chang, Ruobin, Yu, Xiaoquan, Song, Yihu, Huang, Ran
Formato: Online Artículo Texto
Lenguaje:English
Publicado: MDPI 2023
Materias:
Acceso en línea:https://www.ncbi.nlm.nih.gov/pmc/articles/PMC10385391/
https://www.ncbi.nlm.nih.gov/pubmed/37514390
http://dx.doi.org/10.3390/polym15143000
Descripción
Sumario:Cellulose was extracted from coconut shell powder (CSP) as a renewable biomass resource and utilized as a reinforcing material in poly(lactic acid)/poly(butylene succinate) (PLA/PBS) solvent casting films. The extraction process involved delignification and mercerization of CSP. Microscopic investigation of the extracted microfibers demonstrated a reduction in diameter and a rougher surface characteristic compared to the raw CSP. The cellulose prepared in this study exhibited improved thermal stability and higher crystallinity (54.3%) compared to CSP. The morphology of the cycrofractured surface, thermal analysis, mechanical property, and UV transmittance of films were measured and compared. Agglomeration of 3 wt.% of cellulose was observed in PLA/PBS films. The presence of cellulose higher than 1 wt.% in the PLA/PBS decreased the onset decomposition temperature and maximum decomposition temperature of films. However, the films loading 3 wt.% of cellulose had a higher char formation (5.47%) compared to neat PLA/PBS films. The presence of cellulose promoted the formation of non-uniform crystals, while cellulose had a slightly negative impact on crystallinity due to the disruption of polymer chains at lower cellulose content (0.3, 0.5 wt.%). The mechanical strength of PLA/PBS films decreased as the cellulose content increased. Moreover, PLA/PBS film with 3 wt.% of cellulose appeared to show a 3% and 7.5% decrease in transmittance in UVC (275 nm) and UVA (335 nm) regions compared to neat PLA/PBS films while maintaining a certain transparency.