Study on the Effect of Cold Deformation and Heat Treatment on the Properties of Cu-Ag Alloy Wire

The effects of various drawing parameters and annealing processes on the structure and properties of Cu-Ag wires, containing 1 wt% silver, were investigated using specialized equipment including fine wire-drawing machines, very fine wire-drawing machines, heat treatment equipment, tensile testing machines, microcomputer-controlled electronic universal testers, resistance testers, and scanning electron microscopes. The results revealed that continuous drawing of Cu-1%Ag alloy wires led to elongation of the grains, resulting in a uniform and tightly fibrous microstructure. Moreover, the tensile strength of the alloy wire increased from 670 MPa to 783.9 MPa after a single pass with a deformation of 14%. Subsequently, when the wire was drawn at a speed of 500 m/min, the tensile strength further increased to 820.1 MPa. After annealing the Փ0.08 mm Cu-1% Ag alloy wire, an increase in annealing temperature up to 500 °C resulted in the wire’s tensile strength decreasing from 820.1 MPa to 377.5 MPa. Simultaneously, the elongation increased from 1.94% to 15.21%, and the resistivity decreased from 1.931 × 10(−8) Ω·m to 1.723 × 10(−8) Ω·m. Additionally, when annealing was conducted at a rate of 80 m/min, the wire resistivity dropped to 1.635 × 10(−8) Ω·m.