In Situ SEM, TEM, EBSD Characterization of Nucleation and Early Growth of Pure Fe/Pure Al Intermetallic Compounds

The nucleation and growth processes of pure Fe/pure Al intermetallic compounds (IMCs) during heat treatment at 380 °C and 520 °C were observed through in situ scanning electron microscopy (SEM). The size of the IMCs were statistically analyzed using image analysis software. The types and distribution of IMCs were characterized using transmission electron microscopy (TEM) and electron backscattering diffraction (EBSD). The results showed that: at 380 °C, the primary phase of the Fe/Al composite intermetallic compounds was Fe(4)Al(13), formed on the Fe side and habituated with Fe. The IMC was completely transformed from the initial Fe(4)Al(13) to the most stable Fe(2)Al(5), and the Fe(2)Al(5) was the habitus with Fe during the process of holding at 380 °C for 15 min to 60 min. At 380 °C, the initial growth rate of the IMC was controlled by reaction, and the growth rate of the thickness and horizontal dimensions was basically the same as 0.02–0.17 μm/min. When the IMC layer thickness reached 4.5 μm, the growth rate of the thickness changed from reaction control to diffusion control and decreased to 0.007 μm/min. After heat treatment at 520 °C (≤20 min), the growth of IMC was still controlled by the reaction, the horizontal growth rate was 0.53 μm/min, the thickness growth rate was 0.23 μm/min, and the main phase of the IMC was the Fe(2)Al(5) phase at 520 °C/20 min.