Theoretical and Experimental Study of the Photocatalytic Properties of ZnO Semiconductor Nanoparticles Synthesized by Prosopis laevigata

In this work, the photocatalytic activity of nanoparticles (NPs) of zinc oxide synthetized by Prosopis laevigata as a stabilizing agent was evaluated in the degradation of methylene blue (MB) dye under UV radiation. The theoretical study of the photocatalytic degradation process was carried out by a Langmuir–Hinshelwood–Hougen–Watson (LHHW) model. Zinc oxide nanoparticles were synthesized by varying the concentration of natural extract of Prosopis laevigata from 1, 2, and 4% (weight/volume), identifying the samples as ZnO_PL1%, ZnO_PL2%, and ZnO_PL4%, respectively. The characterization of the nanoparticles was carried out by Fourier transform infrared spectroscopy (FT-IR), where the absorption band for the Zn-O vibration at 400 cm(−1) was presented; by ultraviolet–visible spectroscopy (UV–vis) the value of the band gap was calculated, resulting in 2.80, 2.74 and 2.63 eV for the samples ZnO_PL1%, ZnO_PL2%, and ZnO_PL4%, respectively; XRD analysis indicated that the nanoparticles have a hexagonal zincite crystal structure with an average crystal size of 55, 50, and 49 in the sample ZnO_PL1%, ZnO_PL2%, and ZnO_PL4%, respectively. The morphology observed by TEM showed that the nanoparticles had a hemispherical shape, and the ZnO_PL4% sample presented sizes ranging between 29 and 45 nm. The photocatalytic study showed a total degradation of the MB in 150, 120, and 60 min for the samples ZnO_PL1%, ZnO_PL2%, and ZnO_PL4%, respectively. Also, the model explains the experimental observation of the first-order kinetic model in the limit of low concentrations of dye, indicating the influence of the mass transfer processes.