Development of Biodegradable Thermosetting Plastic Using Dialdehyde Pineapple Stem Starch
Starch extracted from pineapple stem waste underwent an environmentally friendly modification process characterized by low-energy consumption. This process resulted in the creation of dialdehyde pineapple stem starch featuring varying aldehyde contents ranging from 10% to 90%. Leveraging these diald...
Autores principales: | , , |
---|---|
Formato: | Online Artículo Texto |
Lenguaje: | English |
Publicado: |
MDPI
2023
|
Materias: | |
Acceso en línea: | https://www.ncbi.nlm.nih.gov/pmc/articles/PMC10536683/ https://www.ncbi.nlm.nih.gov/pubmed/37765686 http://dx.doi.org/10.3390/polym15183832 |
Sumario: | Starch extracted from pineapple stem waste underwent an environmentally friendly modification process characterized by low-energy consumption. This process resulted in the creation of dialdehyde pineapple stem starch featuring varying aldehyde contents ranging from 10% to 90%. Leveraging these dialdehyde starches, thermosetting plastics were meticulously developed by incorporating glycerol as a plasticizer. Concurrently, unmodified pineapple stem starch was employed as a control to produce thermoplastic material under identical conditions. The objective of streamlining the processing steps was pursued by adopting a direct hot compression molding technique. This enabled the transformation of starch powders into plastic sheets without the need for water-based gelatinization. Consequently, the dialdehyde starch-based thermosetting plastics exhibited exceptional mechanical properties, boasting a modulus within the range of 1862 MPa to 2000 MPa and a strength of 15 MPa to 42 MPa. Notably, their stretchability remained relatively modest, spanning from 0.8% to 2.4%. Comparatively, these properties significantly outperformed the thermoplastic counterpart derived from unmodified starch. Tailoring the mechanical performance of the thermosetting plastics was achieved by manipulating the glycerol content, ranging from 30% to 50%. Phase morphologies of the thermoset starch unveiled a uniformly distributed microstructure without any observable starch particles. This stood in contrast to the heterogeneous structure exhibited by the thermoplastic derived from unmodified starch. X-ray diffraction patterns indicated the absence of a crystalline structure within the thermosets, likely attributed to the establishment of a crosslinked structure. The resultant network formation in the thermosets directly correlated with enhanced water resistance. Remarkably, the thermosetting starch originating from pineapple stem starch demonstrated continued biodegradability following a soil burial test, albeit at a notably slower rate when compared to its thermoplastic counterpart. These findings hold the potential to pave the way for the utilization of starch-based products, thereby replacing non-biodegradable petroleum-based materials and contributing to the creation of more enduring and sustainable commodities. |
---|