Development of Mechanical Properties of Stainless Steel 316LN-IG after Cryo-Plastic Deformation

The article deals with increasing the mechanical properties of stainless steel 316 Ln-IG, which is intended for work in cryogenic temperatures (liquid nitrogen and liquid helium), such as conductor conduits for the ITER magnet system. The strength and plastic properties were increased by a combinati...

Descripción completa

Detalles Bibliográficos
Autores principales: Fedoriková, Alica, Petroušek, Patrik, Kvačkaj, Tibor, Kočiško, Róbert, Zemko, Michal
Formato: Online Artículo Texto
Lenguaje:English
Publicado: MDPI 2023
Materias:
Acceso en línea:https://www.ncbi.nlm.nih.gov/pmc/articles/PMC10573374/
https://www.ncbi.nlm.nih.gov/pubmed/37834612
http://dx.doi.org/10.3390/ma16196473
Descripción
Sumario:The article deals with increasing the mechanical properties of stainless steel 316 Ln-IG, which is intended for work in cryogenic temperatures (liquid nitrogen and liquid helium), such as conductor conduits for the ITER magnet system. The strength and plastic properties were increased by a combination of cold and cryo-rolling and heat treatment. The mechanical properties of rolled material were investigated at 293 K, 77 K, and 4.2 K. The work-hardening rate of the steel increased continuously with a lowering of the temperature. The maximum yield strength and ultimate tensile strength were achieved by the cryo-rolling process with a total thickness deformation of 50%. The material properties tested at ambient temperature were 0.2YS = 1050 MPa, UTS = 1200 MPa, and at 4.2 K, the values were 0.2YS = 1804 MPa and UTS = 2081 MPa. Two types of long-term heat treatment were applied after experimental rolling (823 K and 1093 K for 10 h). The highest precipitation hardening of steel was achieved at a temperature of 823 K after 50% deformation. The resulting grain size decreased from the initial 216 μm (before the rolling process) to 70 μm after ambient rolling and 72 μm after cryo-rolling.