Failure Study of BFRP Joints with Two Epoxy Adhesives under Hygrothermal Coupling

Basalt Fibre Reinforced Polymer (BFRP)-bonded structures are lightweight, high strength, economical, and environmentally friendly, which is very advantageous in the civil sector. The aim of this paper is to provide a comprehensive account of the hygrothermal degradation and failure mechanisms of BFR...

Descripción completa

Detalles Bibliográficos
Autores principales:	Niu, Ruitao, Yang, Yang, Lin, Yinghao, Liu, Zhen, Fan, Yisa
Formato:	Online Artículo Texto
Lenguaje:	English
Publicado:	MDPI 2023
Materias:	Article
Acceso en línea:	https://www.ncbi.nlm.nih.gov/pmc/articles/PMC10574937/ https://www.ncbi.nlm.nih.gov/pubmed/37835997 http://dx.doi.org/10.3390/polym15193949

Ejemplares similares

Durability of Two Epoxy Adhesive BFRP Joints Dipped in Seawater under High Temperature Environment
por: Niu, Ruitao, et al.
Publicado: (2023)

Influence of Hydrothermal Aging under Two Typical Adhesives on the Failure of BFRP Single Lap Joint
por: Fan, Yisa, et al.
Publicado: (2022)

Comparison of Mechanical Properties of Ductile/Brittle Epoxy Resin BFRP-AL Joints under Different Immersion Solutions
por: Liu, Haichao, et al.
Publicado: (2023)

Comparative Failure Study of Different Bonded Basalt Fiber-Reinforced Polymer (BFRP)-AL Joints in a Humid and Hot Environment
por: Fan, Yisa, et al.
Publicado: (2021)

Damage of Hygrothermally Conditioned Carbon Epoxy Composites under High-Velocity Impact
por: Liu, Xiang, et al.
Publicado: (2018)

Experimental Investigation of BFRP Tendons under Monotonic and Hysteretic Loadings
por: Wang, Yongwei, et al.
Publicado: (2021)

Residual Flexural Performance of Epoxy Polymer Concrete under Hygrothermal Conditions and Ultraviolet Aging
por: Ma, Dongpeng, et al.
Publicado: (2019)

Hygrothermal Ageing Influence on BVI-Damaged Carbon/Epoxy Coupons under Compression Load
por: Falaschetti, Maria Pia, et al.
Publicado: (2021)

Effect of Service Temperature on Mechanical Properties of Adhesive Joints after Hygrothermal Aging
por: Tan, Wei, et al.
Publicado: (2021)

Effects of Hygrothermal and Salt Mist Ageing on the Properties of Epoxy Resins and Their Composites
por: Wang, Baoming, et al.
Publicado: (2023)

Electrical Properties and Lifetime Prediction of an Epoxy Composite Insulation Material after Hygrothermal Aging
por: Yang, Yan, et al.
Publicado: (2023)

Effect of Hygrothermal Aging on the Mechanical Properties of Fluorinated and Nonfluorinated Clay-Epoxy Nanocomposites
por: Hamim, Salah U., et al.
Publicado: (2014)

Sensing Water Absorption in Hygrothermally Aged Epoxies with Terahertz Time-Domain Spectroscopy
por: Lin, Hungyen, et al.
Publicado: (2021)

Mechanism of Yellowing: Carbonyl Formation during Hygrothermal Aging in a Common Amine Epoxy
por: Krauklis, Andrey E., et al.
Publicado: (2018)

Hygrothermal Aging Characteristics of Silicone-Modified Aging-Resistant Epoxy Resin Insulating Material
por: Wang, Yongqiang, et al.
Publicado: (2021)

Hygrothermal Damage Monitoring of Composite Adhesive Joint Using the Full Spectral Response of Fiber Bragg Grating Sensors
por: Shin, Chow-Shing, et al.
Publicado: (2022)

The Long-Term Interfacial Evolution and Prediction of Carbon- and Glass-Fiber-Reinforced Epoxy Hybrid Rods under a Hygrothermal Environment
por: Liu, Xiaodong, et al.
Publicado: (2023)

Effects of Adhesive Coating on the Hygrothermal Aging Performance of Pultruded CFRP Plates
por: Hao, Xinkai, et al.
Publicado: (2020)

Experimental Study of Mechanical Properties of Epoxy Compounds Modified with Calcium Carbonate and Carbon after Hygrothermal Exposure
por: Rudawska, Anna
Publicado: (2020)

Effect of Hygrothermal Ageing on the Mechanical and Fire Properties of a Flame Retardant Flax Fiber/Epoxy Composite
por: Campana, Charlotte, et al.
Publicado: (2022)

Parameters Influencing Moisture Diffusion in Epoxy-Based Materials during Hygrothermal Ageing—A Review by Statistical Analysis
por: Gillet, Camille, et al.
Publicado: (2022)

Friction Performance of Aged T-BFRP Composite for Bearing Applications
por: Nirmal, Umar
Publicado: (2018)

Bond Stress–Slip Model of BFRP Grid to ECC
por: Deng, Langni, et al.
Publicado: (2022)

Long-Term Durability of Basalt Fiber-Reinforced Polymer (BFRP) Sheets and the Epoxy Resin Matrix under a Wet–Dry Cyclic Condition in a Chloride-Containing Environment
por: Lu, Zhongyu, et al.
Publicado: (2017)

Numerical Modeling of Earthquake-Damaged Circular Bridge Columns Repaired Using Combination of Near-Surface-Mounted BFRP Bars with External BFRP Sheets Jacketing
por: Zeng, Xing-Gui, et al.
Publicado: (2019)

Experimental Study on One-Way BFRP Bar-Reinforced UHPC Slabs under Concentrated Load
por: Xu, Xiaoqing, et al.
Publicado: (2020)

Hygrothermal Behavior, Building Pathology and Durability
por: Freitas, V, et al.
Publicado: (2013)

Hygrothermal climate analysis: An Australian dataset
por: Brambilla, Arianna, et al.
Publicado: (2022)

Climate data for hygrothermal simulations of Brussels
por: Vandemeulebroucke, Isabeau, et al.
Publicado: (2022)

Evaluation of Deformation for Steel Fiber Concrete Beams with BFRP Tendons Eroded by Seawater under Cyclic Loading
por: Zhu, Haitang, et al.
Publicado: (2022)

The Aging Behavior and Life Prediction of CFRP Rods under a Hygrothermal Environment
por: Liu, Xiaodong, et al.
Publicado: (2023)

Delamination Study in Edge Trimming of Basalt Fiber Reinforced Plastics (BFRP)
por: Navarro-Mas, Maria Dolores, et al.
Publicado: (2018)

Hygrothermal Analysis of Laminated Composite Skew Conoids
por: Chaubey, Abhay, et al.
Publicado: (2019)

Degradation of the In-plane Shear Modulus of Structural BFRP Laminates Due to High Temperature
por: Hu, Yu-Jia, et al.
Publicado: (2018)

Analytical and Numerical Approaches for the Design of Concrete Structural Elements with Internal BFRP Reinforcement
por: Zhelyazov, Todor, et al.
Publicado: (2022)

Experimental Study on Shear-Peeling Debonding Behavior of BFRP Sheet-to-Steel Interfaces
por: Xue, Hanyang, et al.
Publicado: (2023)

Adhesive Joint Degradation Due to Hardener-to-Epoxy Ratio Inaccuracy under Varying Curing and Thermal Operating Conditions
por: Szabelski, Jakub, et al.
Publicado: (2022)

Hygrothermal Numerical Simulation Tools Applied to Building Physics
por: Delgado, João M P Q, et al.
Publicado: (2013)

The Influence of Clay Structures to the Hygrothermal Component of the Indoor Environment
por: Diviš, Jakub, et al.
Publicado: (2022)

Effect Mechanism and Simulation of Voids on Hygrothermal Performances of Composites
por: Liu, Zhu, et al.
Publicado: (2022)

Cannot write session to /tmp/vufind_sessions/sess_4up04a84raov7ibh1bd5u5kk1t