Synthesis of Zinc Oxide Doped Magnesium Hydrate and Its Effect on the Flame Retardant and Mechanical Properties of Polypropylene

In this work, an effective flame retardant consisting of nanoscale zinc oxide doped on the surface of hexagonal lamellar magnesium hydrate (ZO@MH) has been successfully synthesized via a hydrothermal process. Approximately 3-methacryloxypropyltrimethoxysilane (KH-570) is chosen as a modifier of ZO@MH for the purpose of enhancing the interfacial interaction between ZO@MH and the polypropylene (PP) matrix and reducing the agglomeration of ZO@MH. Afterwards, ZO@MH and KH-570 modified ZO@MH (KZO@MH) filled PP (PP/ZO@MH and PP/KZO@MH) composites are respectively prepared via the melt blending method. The flame retardant and smoke suppression properties of PP/ZO@MH and PP/KZO@MH composites are estimated by a cone calorimetry test (CCT). The peak value of the heat release rate of the PP/40KZO@MH composite is 327.0 kW/m(2), which is 6.1% and 31.2% lower than that of the PP/40ZO@MH and PP/40MH composites, respectively. The lowest peak values of CO and CO(2) production, 0.008 and 0.62 g/s, also appeared in the PP/40KZO@MH composite, which are 11.1% and 10.1% lower than those of the PP/40ZO@MH composite. Analysis of char residues indicates that nanoscale ZO and modification of KH-570 improve the amount and quality of char residues, which should be the main reason for the good flame retardant and smoke suppression properties of KZO@MH. Impact strength and nominal strain at break results show that the PP matrix is toughened by ZO@MH rather than KZO@MH. Tensile properties and the quantitative interfacial interaction calculated by the Turcsányi equation both prove the reinforcement of KZO@MH on the PP matrix.