Phase patterning of metallic glasses through superfast quenching of ion irradiation-induced thermal spikes
Amorphous metallic glasses (MGs) convert to crystalline solids upon annealing at a high temperature. Such a phase change, however, does not occur with the local melting caused by damage cascades introduced by ion irradiation, although the resulting thermal spikes can reach temperatures > 1000 K....
Autores principales: | Kim, Hyosim, Wang, Tianyao, Gigax, Jonathan, Zare, Arezoo, Lucca, Don A., Hu, Zhihan, Li, Yongchang, Parker, Trevor, Shao, Lin |
---|---|
Formato: | Online Artículo Texto |
Lenguaje: | English |
Publicado: |
Springer Nature Singapore
2023
|
Materias: | |
Acceso en línea: | https://www.ncbi.nlm.nih.gov/pmc/articles/PMC10663422/ https://www.ncbi.nlm.nih.gov/pubmed/37987926 http://dx.doi.org/10.1186/s40580-023-00400-7 |
Ejemplares similares
-
Effect of Helium on Dispersoid Evolution under Self-Ion Irradiation in A Dual-Phase 12Cr Oxide-Dispersion-Strengthened Alloy
por: Kim, Hyosim, et al.
Publicado: (2019) -
Superfast fish show superfast coupling
por: Short, Ben
Publicado: (2022) -
A Novel Microshear Geometry for Exploring the Influence of Void Swelling on the Mechanical Properties Induced by MeV Heavy Ion Irradiation
por: Gigax, Jonathan G., et al.
Publicado: (2022) -
Mn‐Substituted Tunnel‐Type Polyantimonic Acid Confined in a Multidimensional Integrated Architecture Enabling Superfast‐Charging Lithium‐Ion Battery Anodes
por: Wang, Boya, et al.
Publicado: (2020) -
An Intermediate in the evolution of superfast sonic muscles
por: Mok, Hin-Kiu, et al.
Publicado: (2011)