Failure Analysis of Cracked P110 Repaired Tubing Used for Gas Transmission

With green and low-carbon developments in oil fields, an increasing amount of repaired oil tubing is being used as oil and gas transmission pipelines in China. However, due to differences in manufacturing standards between oil tubing and transmission pipelines, there are inevitably some issues durin...

Descripción completa

Detalles Bibliográficos
Autores principales:	Zhang, Shuxin, Xie, Faqin, Wu, Xiangqing, Yan, Xi, Luo, Jinheng, Ma, Xiaoliang, Su, Gege
Formato:	Online Artículo Texto
Lenguaje:	English
Publicado:	MDPI 2023
Materias:	Article
Acceso en línea:	https://www.ncbi.nlm.nih.gov/pmc/articles/PMC10672527/ https://www.ncbi.nlm.nih.gov/pubmed/38005091 http://dx.doi.org/10.3390/ma16227151

Ejemplares similares

The Microstructure Evolution and Mechanical Properties of Rotary Friction Welded Duplex Stainless Steel Pipe
por: Zhang, Shuxin, et al.
Publicado: (2023)

Failure analysis of local settlement induced Q345R bottom plate cracking of crude oil storage tank
por: Shuxin, Zhang, et al.
Publicado: (2022)

Repair of a Cracked Historic Maryan Bell by Gas Welding
por: Bartocha, Dariusz, et al.
Publicado: (2021)

Effect of Duty Cycle on Properties of Al(2)O(3) Ceramic Coatings Fabricated on TiAl Alloy via Cathodic Plasma Electrolytic Deposition
por: Wang, Shaoqing, et al.
Publicado: (2018)

Effect of Titanium and Boron Microalloying on Sulfide Stress Cracking in C110 Casing Steel
por: Luo, Ming, et al.
Publicado: (2020)

Fabrication of High Temperature Oxidation Resistance Nanocomposite Coatings on PEO Treated TC21 Alloy
por: Zhou, Kai, et al.
Publicado: (2019)

Crack Width Evaluation of Cracked Mortar Specimen Using Gas Diffusion Characteristics
por: Lee, Do-Keun, et al.
Publicado: (2023)

A Study on the Influential Factors of Stress Corrosion Cracking in C110 Casing Pipe
por: Wang, Zhe, et al.
Publicado: (2022)

Cleavages along {110} in bcc iron emit dislocations from the curved crack fronts
por: Suzudo, Tomoaki, et al.
Publicado: (2022)

Study on micro crack propagation mechanism of ferrite–pearlite gas transmission pipeline steel with lamellar structure
por: Xu, Taolong, et al.
Publicado: (2022)

A review of crack growth models for near-neutral pH stress corrosion cracking on oil and gas pipelines
por: Sun, Haotian, et al.
Publicado: (2021)

Effect of Initial Crack Position on Crack Propagation Behaviors of Heavy-Duty Transmission Gear
por: Zhang, Yingtao, et al.
Publicado: (2023)

Corrosion Failure Mechanism of Associated Gas Transmission Pipeline
por: Zhao, Weimin, et al.
Publicado: (2018)

Role of Catalyst in Optimizing Fluid Catalytic Cracking Performance During Cracking of H-Oil-Derived Gas Oils
por: Stratiev, Dicho, et al.
Publicado: (2021)

Catalytic Cracking As the Basis for a Potential Detector For Gas Chromatography
por: Bruno, Thomas J.
Publicado: (1987)

Single-layer graphene membranes by crack-free transfer for gas mixture separation
por: Huang, Shiqi, et al.
Publicado: (2018)

Cracking failure of curved hollow tree trunks
por: Huang, Yan-San, et al.
Publicado: (2020)

Use of Genetically Modified Bacteria to Repair Cracks in Concrete
por: Zhang, Zhigang, et al.
Publicado: (2019)

Gas-Modified Pyrolysis Coke for in Situ Catalytic Cracking of Coal Tar
por: Lei, Zhang, et al.
Publicado: (2020)

Crack Width Estimation of Mortar Specimen Using Gas Diffusion Experiment
por: Lee, Do-Keun, et al.
Publicado: (2019)

Modeling the Crack Interference in X80 Oil and Gas Pipeline Weld
por: Cui, Wei, et al.
Publicado: (2023)

Repair of Tube Erosion by Modifying the Tube Extender
por: Liu, Wendy W., et al.
Publicado: (2020)

Correction to ‘Cracking failure of curved hollow tree trunks’
por: Huang, Yan-San, et al.
Publicado: (2020)

Tube Exposure Repair
por: Oana, Stirbu, et al.
Publicado: (2012)

Research on Inner Gas Inflation Improvements in Double-layer Gas-assisted Extrusion of Micro-tubes
por: Luo, Cheng, et al.
Publicado: (2020)

Rendering Rubber Gas Tubing Odorless
Publicado: (1884)

Crack tip shielding observed with high-resolution transmission electron microscopy
por: Adhika, Damar Rastri, et al.
Publicado: (2015)

Assessment of Cracking Widths in a Concrete Wall Based on TIR Radiances of Cracking
por: Su, Tung-Ching
Publicado: (2020)

A Crack Propagation Method for Pipelines with Interacting Corrosion and Crack Defects
por: Xie, Mingjiang, et al.
Publicado: (2022)

The Effect of ZnO on the Failure of PET by Environmental Stress Cracking
por: Barros, Ana Beatriz de Sousa, et al.
Publicado: (2020)

Cracks in the foundation: how COVID-19 showed our failures
por: Bassett, Mary T
Publicado: (2022)

Failure Analysis of Cracking of Cast Aluminum Alloy Manhole Cover
por: Ren, Facai, et al.
Publicado: (2023)

Quantity Effect of Radial Cracks on the Cracking Propagation Behavior and the Crack Morphology
por: Chen, Jingjing, et al.
Publicado: (2014)

Self-protected nitrate reducing culture for intrinsic repair of concrete cracks
por: Erşan, Yusuf Ç., et al.
Publicado: (2015)

Development of Actuators for Repairing Cracks by Coating W Wires with Reactive Multilayers
por: Santos Silva, Gabriel, et al.
Publicado: (2022)

Innovative Calcium Carbonate-Based Products to Repair Cracked Cement Mortars
por: Zuena, Martina, et al.
Publicado: (2022)

Prediction of Fatigue Crack Growth in Gas Turbine Engine Blades Using Acoustic Emission
por: Zhang, Zhiheng, et al.
Publicado: (2018)

Fatigue Crack Monitoring of T-Type Joints in Steel Offshore Oil and Gas Jacket Platform
por: Ali, Liaqat, et al.
Publicado: (2021)

Intradermal Testing Doubles Identification of Allergy among 110 Immunotherapy-Responsive Patients with Eustachian Tube Dysfunction
por: Hurst, David S., et al.
Publicado: (2021)

The Formation Mechanism of the Double Gas Layer in Gas-Assisted Extrusion and Its Influence on Plastic Micro-Tube Formation
por: Liu, Tongke, et al.
Publicado: (2020)

Cannot write session to /tmp/vufind_sessions/sess_cedsmdsvejmicj8v3df0effpab