Cohesive Zone Modeling of the Interface Fracture in Full-Thermoplastic Hybrid Composites for Lightweight Application

With the increasing demand for lightweight and high-performance materials in the automotive and aerospace industries, full-thermoplastic hybrid composites have emerged as a pivotal solution, offering enhanced mechanical properties and design flexibility. This work aims to numerically model the fracture strength in full-thermoplastic hybrid composites made by forming and overmolding organosheets. The mode I fracture was investigated by modeling the behavior of T-joint specimens under a tensile test following the cohesive zone modeling (CZM) approach. The sample was designed to replicate the connection between the laminate and the overmolded part. Double cantilever beam (DCB) specimens were manufactured with organosheets and tested to mode I opening to determine the interlaminar fracture toughness. The fracture toughness out of the mode I test with DCB specimens was used to define the CZM parameters that describe the traction-separation law. Later, due to the particular geometry of the T-join specimens that under tensile load work close to pure mode I, the cohesive parameters were determined by inverse analysis, i.e., calibrating the theoretical models to match experimental results. The fracture resistance T-joint specimens appeared dependent on the fiber-bridging phenomenon during the delamination. In particular, the presence of fiber-bridging visible from the experimental results has been replicated by virtual analyses, and it is observed that it leads to a higher energy value before the interface’s complete breakage. Moreover, a correspondence between the mode I fracture toughness of the DCB specimen and T-joint specimens was observed.