In vitro performance of an autocured universal adhesive system in bonding to dentin

BACKGROUND: The successful integration of resin-based dental adhesives significantly impacts restorative dentistry, providing efficient and aesthetically pleasing caries treatments. Among various adhesives, one-step self-etching adhesives (1-SEAs) have gained popularity due to their simplicity and short application time. However, concerns have been raised regarding their bonding performance and marginal adaptation characteristics, which differ from two-step self-etching adhesives (2-SEAs) and three-step etch-and-rinse adhesives. Additionally, light-cured bonding materials may encounter challenges in deep cavities and inaccessible areas, necessitating extended light irradiation time. Autocured bonding materials are a potential solution, but limited comparative studies have been conducted on their performance. METHODS: In this in vitro study, we evaluated a new autocured universal bonding material (Bondmer Lightless 2) and compared the results with recent light-cured bonding materials. Microshear bond strength (μSBS) tests were performed on 25 human molars using five different combinations of adhesives and composite resins: Bondmer Lightless 2 with Estelite Bulk Fill Flow (BE group), Bondmer Lightless 2 with a prototype composite resin (BO group), Prime&Bond Universal with SDR flow + (PS group), Scotchbond Universal with Filtek Bulk Fill (SF group), and G-Premio Bond with Gracefil BulkFlo (GG group). The bond strengths and failure modes were assessed using a universal testing machine and scanning electron microscope (SEM), respectively. Marginal adaptation was evaluated using swept-source optical coherence tomography (SS-OCT) and confocal laser scanning microscopy (CLSM) on 40 sound bovine maxillary incisors. RESULTS: The μSBS test showed no significant differences in bond strength among the tested groups. Most failure modes were observed at the bond interface between the adhesive and the dentin. The autocured bonding material demonstrated significantly higher marginal adaptation (SI%) than PS, SF, and GG. The CLSM images corresponded with gaps observed in the SS-OCT images, indicating improved marginal sealing in the autocured group. CONCLUSIONS: The new autocured universal bonding material exhibited comparable bond strength to a conventional light-cured material while demonstrating a superior marginal adaptation level. This finding suggested that the autocured material could be a valuable alternative, especially when extended light irradiation would pose a challenge. Further clinical studies would be warranted to evaluate the performance of the autocured bonding material in actual restorative dental practice.