Design for improving corrosion resistance of duplex stainless steels by wrapping inclusions with niobium armour
Unavoidable nonmetallic inclusions generated in the steelmaking process are fatal defects that often cause serious corrosion failure of steel, leading to catastrophic accidents and huge economic losses. Over the past decades, extensive efforts have been made to address this difficult issue, but none...
Autores principales: | Zhang, Shucai, Feng, Hao, Li, Huabing, Jiang, Zhouhua, Zhang, Tao, Zhu, Hongchun, Lin, Yue, Zhang, Wei, Li, Guoping |
---|---|
Formato: | Online Artículo Texto |
Lenguaje: | English |
Publicado: |
Nature Publishing Group UK
2023
|
Materias: | |
Acceso en línea: | https://www.ncbi.nlm.nih.gov/pmc/articles/PMC10689471/ https://www.ncbi.nlm.nih.gov/pubmed/38036658 http://dx.doi.org/10.1038/s41467-023-43752-8 |
Ejemplares similares
-
Microbiologically Influenced Corrosion of 2707 Hyper-Duplex Stainless Steel by Marine Pseudomonas aeruginosa Biofilm
por: Li, Huabing, et al.
Publicado: (2016) -
Relationship between Microstructure and Corrosion Behavior of Martensitic High Nitrogen Stainless Steel 30Cr15Mo1N at Different Austenitizing Temperatures
por: Jiang, Zhouhua, et al.
Publicado: (2017) -
Corrosion Resistance of GMAW Duplex Stainless Steels Welds
por: Miranda-Pérez, Argelia Fabiola, et al.
Publicado: (2023) -
Corrosion Inhibition Mechanism of Ultra-High-Temperature Acidizing Corrosion Inhibitor for 2205 Duplex Stainless Steel
por: Li, Danping, et al.
Publicado: (2023) -
Effect of Secondary Phase Precipitation on the Corrosion Behavior of Duplex Stainless Steels
por: Chan, Kai Wang, et al.
Publicado: (2014)