Facile Fabrication of Uniform Polyaniline Nanotubes with Tubular Aluminosilicates as Templates

The uniform polyaniline (PANI) nanotubes, with inner diameter, outer diameter, and tubular thickness of 40, 60, and 10 nm, respectively, were prepared successfully by using natural tubular aluminosilicates as templates. The halloysite nanotubes were coated with PANI via the in situ chemical oxidatio...

Descripción completa

Detalles Bibliográficos
Autores principales: Zhang, Long, Liu, Peng
Formato: Online Artículo Texto
Lenguaje:English
Publicado: Springer 2008
Materias:
Nano Express
Acceso en línea:https://www.ncbi.nlm.nih.gov/pmc/articles/PMC3244873/
http://dx.doi.org/10.1007/s11671-008-9155-z
_version_ 1782219767149494272
author Zhang, Long
Liu, Peng
author_facet Zhang, Long
Liu, Peng
author_sort Zhang, Long
collection PubMed
description The uniform polyaniline (PANI) nanotubes, with inner diameter, outer diameter, and tubular thickness of 40, 60, and 10 nm, respectively, were prepared successfully by using natural tubular aluminosilicates as templates. The halloysite nanotubes were coated with PANI via the in situ chemical oxidation polymerization. Then the templates were etched with HCl/HF solution. The PANI nanotubes were characterized using FTIR, X-ray diffraction, and transmission electron microscopy. The conductivity of the PANI nanotubes was found to be 1.752 × 10(−5)(Ω·cm)(−1).
format Online
Article
Text
id pubmed-3244873
institution National Center for Biotechnology Information
language English
publishDate 2008
publisher Springer
record_format MEDLINE/PubMed
spelling pubmed-32448732011-12-22 Facile Fabrication of Uniform Polyaniline Nanotubes with Tubular Aluminosilicates as Templates Zhang, Long Liu, Peng Nanoscale Res Lett Nano Express The uniform polyaniline (PANI) nanotubes, with inner diameter, outer diameter, and tubular thickness of 40, 60, and 10 nm, respectively, were prepared successfully by using natural tubular aluminosilicates as templates. The halloysite nanotubes were coated with PANI via the in situ chemical oxidation polymerization. Then the templates were etched with HCl/HF solution. The PANI nanotubes were characterized using FTIR, X-ray diffraction, and transmission electron microscopy. The conductivity of the PANI nanotubes was found to be 1.752 × 10(−5)(Ω·cm)(−1). Springer 2008-08-17 /pmc/articles/PMC3244873/ http://dx.doi.org/10.1007/s11671-008-9155-z Text en Copyright ©2008 to the authors
spellingShingle Nano Express
Zhang, Long
Liu, Peng
Facile Fabrication of Uniform Polyaniline Nanotubes with Tubular Aluminosilicates as Templates
title Facile Fabrication of Uniform Polyaniline Nanotubes with Tubular Aluminosilicates as Templates
title_full Facile Fabrication of Uniform Polyaniline Nanotubes with Tubular Aluminosilicates as Templates
title_fullStr Facile Fabrication of Uniform Polyaniline Nanotubes with Tubular Aluminosilicates as Templates
title_full_unstemmed Facile Fabrication of Uniform Polyaniline Nanotubes with Tubular Aluminosilicates as Templates
title_short Facile Fabrication of Uniform Polyaniline Nanotubes with Tubular Aluminosilicates as Templates
title_sort facile fabrication of uniform polyaniline nanotubes with tubular aluminosilicates as templates
topic Nano Express
url https://www.ncbi.nlm.nih.gov/pmc/articles/PMC3244873/
http://dx.doi.org/10.1007/s11671-008-9155-z
work_keys_str_mv AT zhanglong facilefabricationofuniformpolyanilinenanotubeswithtubularaluminosilicatesastemplates
AT liupeng facilefabricationofuniformpolyanilinenanotubeswithtubularaluminosilicatesastemplates

Ejemplares similares