Sputter-prepared (001) BiFeO(3) thin films with ferromagnetic L1(0)-FePt(001) electrode on glass substrates

Highly textured BiFeO(3)(001) films were formed on L1(0)-FePt(001) bottom electrodes on glass substrates by sputtering at reduced temperature of 400°C. Good electric polarization 2P(r) = 80 and 95 μC/cm(2), comparable to that of the reported epitaxial films, and coercivity E(c) = 415 and 435 kV/cm a...

Descripción completa

Detalles Bibliográficos
Autores principales: Chang, Huang-Wei, Yuan, Fu-Te, Shih, Chih-Wei, Ku, Ching-Shun, Chen, Ping-Han, Wang, Chang-Ren, Chang, Wen-Cheng, Jen, Shien-Uang, Lee, Hsin-Yi
Formato: Online Artículo Texto
Lenguaje:English
Publicado: Springer 2012
Materias:
Nano Express
Acceso en línea:https://www.ncbi.nlm.nih.gov/pmc/articles/PMC3477037/
https://www.ncbi.nlm.nih.gov/pubmed/22863085
http://dx.doi.org/10.1186/1556-276X-7-435
Descripción
Sumario:Highly textured BiFeO(3)(001) films were formed on L1(0)-FePt(001) bottom electrodes on glass substrates by sputtering at reduced temperature of 400°C. Good electric polarization 2P(r) = 80 and 95 μC/cm(2), comparable to that of the reported epitaxial films, and coercivity E(c) = 415 and 435 kV/cm are achieved in the samples with 20-nm- and 30-nm-thick electrodes. The BiFeO(3)(001) films show different degrees of compressive strain. The relation between the variations of strain and 2P(r) suggests that the enhancement of 2P(r) resulted from the strain-induced rotation of spontaneous polarization. The presented results open possibilities for the applications based on electric-magnetic interactions.

Ejemplares similares