Effect of NaF, SnF(2), and TiF(4) Toothpastes on Bovine Enamel and Dentin Erosion-Abrasion In Vitro

The aim of this study was to compare the effect of toothpastes containing TiF(4), NaF, and SnF(2) on tooth erosion-abrasion. Bovine enamel and dentin specimens were distributed into 10 groups (n = 12): experimental placebo toothpaste (no F); NaF (1450 ppm F); TiF(4) (1450 ppm F); SnF(2) (1450 ppm F); SnF(2) (1100 ppm F) + NaF (350 ppm F); TiF(4) (1100 ppm F) + NaF (350 ppm F); commercial toothpaste Pro-Health (SnF(2)—1100 ppm F + NaF—350 ppm F, Oral B); commercial toothpaste Crest (NaF—1.500 ppm F, Procter & Gamble); abrasion without toothpaste and only erosion. The erosion was performed 4 × 90 s/day (Sprite Zero). The toothpastes' slurries were applied and the specimens abraded using an electric toothbrush 2 × 15 s/day. Between the erosive and abrasive challenges, the specimens remained in artificial saliva. After 7 days, the tooth wear was evaluated using contact profilometry (μm). The experimental toothpastes with NaF, TiF(4), SnF(2), and Pro-Health showed a significant reduction in enamel wear (between 42% and 54%). Pro-Health also significantly reduced the dentin wear. The toothpastes with SnF(2)/NaF and TiF(4)/NaF showed the best results in the reduction of enamel wear (62–70%) as well as TiF(4), SnF(2), SnF(2)/NaF, and TiF(4)/NaF for dentin wear (64–79%) (P < 0.05). Therefore, the experimental toothpastes containing both conventional and metal fluoride seem to be promising in reducing tooth wear.