In vivo wear performance of highly cross-linked polyethylene vs. yttria stabilized zirconia and alumina stabilized zirconia at a mean seven-year follow-up

BACKGROUND: Zirconia was introduced as an alternative to alumina for use in the femoral head. The yttria stabilized zirconia material was improved by adding alumina. We evaluated highly cross-linked polyethylene wear performance of zirconia in total hip arthroplasty. The hypothesis was that alumina stabilized zirconia could decrease highly cross-linked polyethylene wear. METHODS: Highly cross-linked polyethylene wear was measured with a computerized method (PolyWare) in 91 hips. The steady-state wear rates were measured based on the radiographs from the first year postoperatively to the final follow-up and were compared between hips with yttria stabilized zirconia and alumina stabilized zirconia. RESULTS: The steady-state wear rate of highly cross-linked polyethylene against zirconia was 0.02 mm/year at a mean follow-up of 7 years. No significant difference was observed between groups with yttria stabilized zirconia and alumina stabilized zirconia. CONCLUSIONS: Addition of alumina to the zirconia material failed to show further reduction of highly cross-linked polyethylene wear and our hypothesis was not verified.