Effect of thermal cycling on denture base and autopolymerizing reline resins

OBJECTIVE: This study evaluated the fracture toughness (FT) of denture base and autopolymerizing reline resins, with and without thermocycling (T). MATERIAL AND METHODS: Specimens of each material (denture base acrylic resin - Lucitone 550 - L; autopolymerizing reline resins - Ufi Gel Hard-UH, Tokuyama Rebase II-TR, New Truliner- NT and Kooliner-K), were produced, notched and divided into two groups (n=10): CG (control group of autopolymerizing reline resins and L): FT tests were performed after polymerization; TG (thermocycled group): FT tests were performed after T (5ºC and 55ºC for 5,000 cycles). RESULTS: Results (MPa.m((1/2))) were analyzed by two-way ANOVA and Tukey's test (p=0.05). L exhibited the highest FT mean values in both groups (CG - 2.33; TG - 2.17). For the CG groups, NT showed the highest FT (1.64) among the autopolymerizing reline resins, and K the lowest (1.04). After T, when the autopolymerizing reline resins were compared, a statistically significant difference in FT was found only between the NT (1.46) and TR (1.00). CONCLUSIONS: Thermocycling increased the FT of K and did not influence the FT of L, UH, TR and NT.