Physical Properties of Polyamide-12 versus PMMA Denture Base Material
Objectives. Polyamide-12 (PA) is a flexible material suited for denture bases and clasping. This study investigated its potential aging effects with a focus on surface roughness, color stability, and elasticity. Methods. PA specimens (Valplast) of 40 × 10 × 2 mm and equally measuring PMMA specimens...
Autores principales: | , , , |
---|---|
Formato: | Online Artículo Texto |
Lenguaje: | English |
Publicado: |
Hindawi Publishing Corporation
2014
|
Materias: | |
Acceso en línea: | https://www.ncbi.nlm.nih.gov/pmc/articles/PMC3966424/ https://www.ncbi.nlm.nih.gov/pubmed/24734225 http://dx.doi.org/10.1155/2014/150298 |
Sumario: | Objectives. Polyamide-12 (PA) is a flexible material suited for denture bases and clasping. This study investigated its potential aging effects with a focus on surface roughness, color stability, and elasticity. Methods. PA specimens (Valplast) of 40 × 10 × 2 mm and equally measuring PMMA specimens (Palapress) as control were fabricated. Color changes after storage in air, water, coffee, and red wine (n = 10) were measured using the CIE L*a*b* color specification. Elasticity after thermocycling (1000, 3000, and 7000 cycles, n = 15) was measured by three-point bending testing. Mean surface roughness (Ra) was determined after storage in the liquids mentioned above and thermocycling (n = 10). Results. Tukey's HSD test (P < 0.05) revealed statistically significant color changes of PA in red wine (ΔE = 4.27 after 12 days, ΔE = 6.90 after 12 days) and coffee (ΔE = 3.93 after 36 days) but no color changes in PMMA. Elastic modulus of PA was 845 MPa and not affected by thermocycling (Tukey's HSD test, P > 0.81). Dry specimens showed significantly decreased elasticity (P < 0.001). Mean surface roughness (PA 0.20 μm, PMMA 0.28 μm) did not change significantly after thermocycling or storage (Mann-Whitney U-test, 0.16 < P < 0.65). Significance. PA exhibited a higher susceptibility to discoloration than PMMA. Neither surface roughness nor elasticity of PA was altered by artificial aging. |
---|