Comparative Study of the Effect of Acid Etching on Enamel Surface Roughness between Pumiced and Non-pumiced Teeth

BACKGROUND: The objective was to perform a comparative analysis of the effect of acid etching on enamel roughness between pumiced and non-pumiced teeth. MATERIALS AND METHODS: The sample was composed of 32 dental surfaces divided into two groups: Group 1-16 surfaces having received pumice prophylaxi...

Descripción completa

Detalles Bibliográficos
Autores principales: Abreu, Lucas Guimarães, Paiva, Saul Martins, Pretti, Henrique, Lages, Elizabeth Maria Bastos, Júnior, João Batista Novães, Ferreira, Ricardo Alberto Neto
Formato: Online Artículo Texto
Lenguaje:English
Publicado: Dentmedpub Research and Printing Co 2015
Materias:
Acceso en línea:https://www.ncbi.nlm.nih.gov/pmc/articles/PMC4589700/
https://www.ncbi.nlm.nih.gov/pubmed/26435607
Descripción
Sumario:BACKGROUND: The objective was to perform a comparative analysis of the effect of acid etching on enamel roughness between pumiced and non-pumiced teeth. MATERIALS AND METHODS: The sample was composed of 32 dental surfaces divided into two groups: Group 1-16 surfaces having received pumice prophylaxis; and Group 2-16 surfaces not having received pumice prophylaxis. The teeth were kept in saline until the first record of surface roughness prior to etching. For each surface, a roughness graph was obtained through trials using a surface roughness tester. This procedure was repeated two more times at different locations for a total of three readings which, later, were converted in a mean value. The teeth were then acid etched with a 37% phosphoric acid for 60 s, rinsed with water, air dried, and tested with the roughness tester again using the same protocol described for baseline. The Quantikov image analysis program was used to measure the length of the graphs. The average value of the lengths was recorded for each surface before and after etching. The increase in roughness caused by acid etching was calculated and compared between groups. RESULTS: The mean increase in roughness caused by the etching was 301 µm (11.37%) in Group 1 and 214 µm (8.33%) in Group 2. No statistically significant difference was found between samples with and without pumice prophylaxis (P = 0.283). CONCLUSION: The present study showed that the effect of acid etching on enamel roughness was not significantly affected by prior pumice prophylaxis.