Oxidation mechanism of T91 steel in liquid lead-bismuth eutectic: with consideration of internal oxidation
Clarification of the microscopic events that occur during oxidation is of great importance for understanding and consequently controlling the oxidation process. In this study the oxidation product formed on T91 ferritic/martensitic steel in oxygen saturated liquid lead-bismuth eutectic (LBE) at 823 ...
Autores principales: | Ye, Zhongfei, Wang, Pei, Dong, Hong, Li, Dianzhong, Zhang, Yutuo, Li, Yiyi |
---|---|
Formato: | Online Artículo Texto |
Lenguaje: | English |
Publicado: |
Nature Publishing Group
2016
|
Materias: | |
Acceso en línea: | https://www.ncbi.nlm.nih.gov/pmc/articles/PMC5062345/ https://www.ncbi.nlm.nih.gov/pubmed/27734928 http://dx.doi.org/10.1038/srep35268 |
Ejemplares similares
-
Microstructural Investigation of LME Crack Initiated in Ferritic/Martensitic Steel T91 Loaded in Liquid Lead-Bismuth Eutectic at 300 °C
por: Halodová, Patricie, et al.
Publicado: (2018) -
Effect of Silicon on Dynamic/Static Corrosion Resistance of T91 in Lead–Bismuth Eutectic at 550 °C
por: Li, Ji, et al.
Publicado: (2022) -
Characterization of mechanical strain induced by lead-bismuth eutectic (LBE) freezing in stainless steel cup
por: Odaira, Naoya, et al.
Publicado: (2020) -
Lead-Bismuth Eutectic: Atomic and Micro-Scale Melt Evolution
por: Montanari, Roberto, et al.
Publicado: (2019) -
Effect of Applied Stress on T91 Steel Performance in Liquid Lead at 400 °C
por: Hojná, Anna, et al.
Publicado: (2018)