Comparison of Polyethylene Wear before and after Hip Revision with Liner Exchange Fixed with the Original Locking Mechanism

OBJECTIVE: To compare the wear of conventional ultra-high molecular weight polyethylene (CUHMWPE) and highly cross-linked polyethylene (HCLPE) in hip revision with liner exchange fixed with original locking mechanism using analysis of history medical data. METHODS: From Jan. 1, 2000, to Dec. 31, 2007, 26 patients (with 29 involved hips) underwent liner exchange revision fixed with the original locking mechanism due to wear of CUHMWPE and/or osteolysis. The mean age was 53 ± 9 years at the time of the primary total hip arthroplasty (THA) and 64 ± 9 years at the revision. The exchanged liners (Marathon, Depuy) were made of HCLPE. Annual X-rays were used to measure linear wear and osteolysis. The annual linear penetration was measured using PolyWare® software (Draftware Inc.). Annual Harris Hip Scores(HSS) were recorded. RESULTS: The mean follow-up time between the primary and revision THAs was 11 ± 2 years and 8 ± 2 years after revision. The mean Harris Hip Score(HHS) before primary THA, 1 year after primary THA, before revision and 1 year after revision was 43±5, 85±5, 71±6, 83±7 individually. The mean penetration of the CUHMWPE and HCLPE liners occurring in the first year were 0.44 ± 0.28 mm and 0.38 ± 0.14 mm, respectively (p = 0.211). The mean annual linear penetration of CUHMWPE and HCLPE from the second year onward were 0.29±0.09 mm and 0.08 ± 0.03 mm respectively (p <0.01). All THAs with CUHMWPE showed osteolysis on acetabular and/or femoral side before revision. No HCLPE liner showed osteolysis at the last follow-up. Conclusion: The CUHMWPE liner had a significantly higher wear rate than did the HCLPE liner. The HCLPE liner showed a satisfactory liner penetration rate after revision with isolated liner exchange fixed with the original locking mechanism.