Electric field control of magnetization reorientation in Co/Pb (Mg(1/3)Nb(2/3))-PbTiO(3) heterostructure

Herein, we demonstrated an apparent electric field control of magnetization reorientation at room temperature, through a strain-mediated magnetoelectric coupling in ferromagnetic/ferroelectric (FM/FE) multiferroic heterostructure. As the applied electric field increased, the magnetization tended to deviate from the original direction, which was induced by nonlinear strain vs electric-field behavior from the ferroelectric substrates. Ferromagnetic resonance showed that the in-plane magnetic easy axis of the Co film was shifted sharply with electric field E = 10 kV/cm, which indicates that the in-plane uniaxial magnetic anisotropy of the Co film can be inverted via the application of an electric field. These results demonstrated that converse magnetoelectric effect in the FM/FE heterostructure was indeed a feasible method to control magnetization orientation in technologically relevant ferromagnetic thin films at room temperature.