Concrete Cracking Prediction Including the Filling Proportion of Strand Corrosion Products

The filling of strand corrosion products during concrete crack propagation is investigated experimentally in the present paper. The effects of stirrups on the filling of corrosion products and concrete cracking are clarified. A prediction model of crack width is developed incorporating the filling p...

Descripción completa

Detalles Bibliográficos
Autores principales:	Wang, Lei, Dai, Lizhao, Zhang, Xuhui, Zhang, Jianren
Formato:	Online Artículo Texto
Lenguaje:	English
Publicado:	MDPI 2016
Materias:	Article
Acceso en línea:	https://www.ncbi.nlm.nih.gov/pmc/articles/PMC5344591/ https://www.ncbi.nlm.nih.gov/pubmed/28772367 http://dx.doi.org/10.3390/ma10010006

Ejemplares similares

Concrete Cover Cracking and Reinforcement Corrosion Behavior in Concrete with New-to-Old Concrete Interfaces
por: Zhang, Juhui, et al.
Publicado: (2023)

Modelling of Corrosion-Induced Concrete Cover Cracking Due to Chloride Attacking
por: Lun, Pei-Yuan, et al.
Publicado: (2021)

Fractal Characteristics of Corrosion-Induced Cracks in Reinforced Concrete
por: Ji, Haodong, et al.
Publicado: (2020)

A Prediction Model of the Concrete Cracking Induced by the Non-Uniform Corrosion of the Steel Reinforcement
por: ZHU, Wenjun, et al.
Publicado: (2020)

Concrete Protective Layer Cracking Caused by Non-Uniform Corrosion of Reinforcements
por: Zhang, Lu, et al.
Publicado: (2019)

A Cracking Model for Reinforced Concrete Cover, Taking Account of the Accumulation of Corrosion Products in the ITZ Layer, and Including Computational and Experimental Verification
por: Krykowski, Tomasz, et al.
Publicado: (2020)

A Monitoring Method Based on FBG for Concrete Corrosion Cracking
por: Mao, Jianghong, et al.
Publicado: (2016)

Prediction of Corrosion-Induced Longitudinal Cracking Time of Concrete Cover Surface of Reinforced Concrete Structures under Load
por: Wang, Jian, et al.
Publicado: (2022)

Water Transport through Cracked Concrete Structures—Effect of Mixture Proportion on Separating Crack Geometry and Permeability
por: Mengel, Lena, et al.
Publicado: (2022)

Corrosion Product Film-Induced Stress Facilitates Stress Corrosion Cracking
por: Wang, Wenwen, et al.
Publicado: (2015)

Numerical Investigation on Lateral Confinement Effects on Concrete Cracking Induced by Rebar Corrosion
por: Choe, Gyeongcheol, et al.
Publicado: (2020)

Cracking in Reinforced Concrete Cross-Sections Due to Non-Uniformly Distributed Corrosion
por: German, Magdalena, et al.
Publicado: (2023)

Quantification of the Influence of Concrete Width per Fiber Strand on the Splitting Crack Failure of Textile Reinforced Concrete (TRC)
por: Beßling, Markus, et al.
Publicado: (2022)

Corrosion Behavior of Steel Reinforcement in Concrete with Recycled Aggregates, Fly Ash and Spent Cracking Catalyst
por: Gurdián, Hebé, et al.
Publicado: (2014)

Use of Non-Linear Ultrasonic Techniques to Detect Cracks Due to Steel Corrosion in Reinforced Concrete Structures
por: Climent, Miguel Ángel, et al.
Publicado: (2019)

Steel Corrosion Evaluation of Basalt Fiber RPC Affected by Crack and Steel-Concrete Interface Damage Using Electrochemical Methods
por: Liu, Hanbing, et al.
Publicado: (2020)

Effects of Transverse Crack on Chloride Ions Diffusion and Steel Bars Corrosion Behavior in Concrete under Electric Acceleration
por: Du, Fengyin, et al.
Publicado: (2019)

A probabilistic computational framework for the prediction of corrosion-induced cracking in large structures
por: Qian, Guofeng, et al.
Publicado: (2022)

Analytical Hysteretic Behavior of Square Concrete-Filled Steel Tube Pier Columns under Alternate Sulfate Corrosion and Freeze-Thaw Cycles
por: Zhang, Tong, et al.
Publicado: (2022)

A Crack Propagation Method for Pipelines with Interacting Corrosion and Crack Defects
por: Xie, Mingjiang, et al.
Publicado: (2022)

Filling Capacity Evaluation of Self-Compacting Concrete in Rock-Filled Concrete
por: Liu, Wenju, et al.
Publicado: (2019)

Corrosion-Effected Bond Behavior between PVA-Fiber-Reinforced Concrete and Steel Rebar under Chloride Environment
por: Zhang, Xuhui, et al.
Publicado: (2023)

Analysis of Carbonation Behavior of Cracked Concrete
por: Guo, Qun, et al.
Publicado: (2022)

Review on Microbially Influenced Concrete Corrosion
por: Wang, Dongsheng, et al.
Publicado: (2023)

Modeling Corrosion Product Film Formation and Hydrogen Diffusion at the Crack Tip of Austenitic Stainless Steel
por: Yang, Fuqiang, et al.
Publicado: (2023)

Electromagnetic Metrology on Concrete and Corrosion
por: Kim, Sung, et al.
Publicado: (2011)

Corrosion of steel in concrete : prevention, diagnosis, repair /
Publicado: (2004)

Use of Genetically Modified Bacteria to Repair Cracks in Concrete
por: Zhang, Zhigang, et al.
Publicado: (2019)

Assessment of Cracking Widths in a Concrete Wall Based on TIR Radiances of Cracking
por: Su, Tung-Ching
Publicado: (2020)

Prediction of Crack Width in RC Piles Exposed to Local Corrosion in Chloride Environment
por: Shao, Wei, et al.
Publicado: (2023)

Crack Evaluation of Concrete Using Mechanochromic Sensor
por: Pyeon, Sujeong, et al.
Publicado: (2023)

Prediction and Analysis of the Residual Capacity of Concrete-Filled Steel Tube Stub Columns under Axial Compression Subjected to Combined Freeze–Thaw Cycles and Acid Rain Corrosion
por: Zhang, Tong, et al.
Publicado: (2019)

Bond Properties of Carbon Fiber Reinforced Polymer and Corrosion-Cracked Reinforced Concrete Interface: Experimental Test and Nonlinear Degenerate Interface Law
por: Gong, Yongzhi, et al.
Publicado: (2021)

Degradation of Axial Ultimate Load-Bearing Capacity of Circular Thin-Walled Concrete-Filled Steel Tubular Stub Columns after Corrosion
por: Zhang, Fengjie, et al.
Publicado: (2020)

The Localized Corrosion and Stress Corrosion Cracking of a 6005A-T6 Extrusion Profile
por: Ma, Jijun, et al.
Publicado: (2021)

Corrosion Crack Morphology and Creep Analysis of Members Based on Meso-Scale Corrosion Penetration
por: Zeng, Bin, et al.
Publicado: (2022)

Stress Corrosion Cracking of Additively Manufactured Alloy 625
por: Cabrini, Marina, et al.
Publicado: (2021)

Microscopic Analysis of Steel Corrosion Products in Seawater and Sea-Sand Concrete
por: Wang, Gang, et al.
Publicado: (2019)

Microstructure and Pitting Corrosion of Austenite Stainless Steel after Crack Arrest
por: Zhang, Zhuwu, et al.
Publicado: (2019)

Experimental Behavior of Cracked Reinforced Concrete Columns Strengthened with Reinforced Concrete Jacketing
por: Mohamed Sayed, Ahmed, et al.
Publicado: (2020)

Cannot write session to /tmp/vufind_sessions/sess_66n59bvffmefrqhgm0b0t1kteb