Deformation of nickel-titanium closed coil springs: an in vitro study

OBJECTIVE: The aim of this paper was to determine the amount of deformation in four commercial brands of nickel-titanium closed springs. METHODS: A total of 130 springs were divided into 13 subgroups, according to their features and manufacturers (Morelli, Orthometric, Ormco and GAC) and activated f...

Descripción completa

Detalles Bibliográficos
Autores principales: Vieira, Camilla Ivini Viana, Reis, José Maurício dos Santos Nunes, Vaz, Luiz Geraldo, Martins, Lídia Parsekian, Martins, Renato Parsekian
Formato: Online Artículo Texto
Lenguaje:English
Publicado: Dental Press International 2017
Materias:
Acceso en línea:https://www.ncbi.nlm.nih.gov/pmc/articles/PMC5398841/
https://www.ncbi.nlm.nih.gov/pubmed/28444020
http://dx.doi.org/10.1590/2177-6709.22.1.038-046.oar
Descripción
Sumario:OBJECTIVE: The aim of this paper was to determine the amount of deformation in four commercial brands of nickel-titanium closed springs. METHODS: A total of 130 springs were divided into 13 subgroups, according to their features and manufacturers (Morelli, Orthometric, Ormco and GAC) and activated from 100% to 1000% of the effective length of the nickel-titanium portion present at the spring, at 37 °C. Deactivation data were plotted and deformation was found graphically. The values were compared by analysis of variance and Tukey's post-hoc test. RESULTS: Springs manufactured by Morelli had the same amount of deformation when they were activated up to 700% of Y activation; springs by Orthometric had the same amount of deformation up to 600-700% of Y; springs by Ormco had the same amount of deformation up to 700-800% of Y; and finally, the majority of springs by GAC had similar deformation up to 800%-1000% of activation. All springs tested could be activated up to 700% without rupture. CONCLUSIONS: Most subgroups were similarly deformed up to 700% of activation, without rupture of springs. Subgroups 4B, 4C, 4D and 4E showed the same amount of deformation up to 1000% of activation without any rupture at all.