Behavior of Plain Concrete of a High Water-Cement Ratio after Freeze-Thaw Cycles

An experimental study of plain concrete specimens of water-cement ratio 0.55, subjected to 0, 15, 25, 40, 50 and 75 cycles of freeze-thaw was completed. The dynamic modulus of elasticity (DME), weight loss, compressive strength, tensile strength, flexural strength, cleavage strength and stress-strai...

Descripción completa

Detalles Bibliográficos
Autores principales:	Shang, Huai-Shuai, Yi, Ting-Hua, Song, Yu-Pu
Formato:	Online Artículo Texto
Lenguaje:	English
Publicado:	MDPI 2012
Materias:	Article
Acceso en línea:	https://www.ncbi.nlm.nih.gov/pmc/articles/PMC5449020/ http://dx.doi.org/10.3390/ma5091698

Ejemplares similares

Freeze-Thaw Durability of Air-Entrained Concrete
por: Shang, Huai-Shuai, et al.
Publicado: (2013)

Effect of Fast Freeze-Thaw Cycles on Mechanical Properties of Ordinary-Air-Entrained Concrete
por: Shang, Huai-shuai, et al.
Publicado: (2014)

Bond Behavior of Steel Bars in Concrete Confined with Stirrups under Freeze–Thaw Cycles
por: Liu, Guirong, et al.
Publicado: (2022)

Bond Behavior of Reinforced Concrete Considering Freeze–Thaw Cycles and Corrosion of Stirrups
por: Liu, Shuo, et al.
Publicado: (2021)

Residual TRM-to-Concrete Bond after Freeze–Thaw Cycles
por: Askouni, Paraskevi D., et al.
Publicado: (2021)

Concrete Durability after Load Damage and Salt Freeze–Thaw Cycles
por: Zhou, Jiguo, et al.
Publicado: (2022)

Investigation on mechanical properties deterioration of concrete subjected to freeze–thaw cycles
por: Xie, Ruifeng, et al.
Publicado: (2022)

Fracture Behavior of Concrete under Chlorine Salt Attack Exposed to Freeze–Thaw Cycles Environment
por: Li, Wenhao, et al.
Publicado: (2023)

Experimental Study on Freezing and Thawing Cycles of Shrinkage-Compensating Concrete with Double Expansive Agents
por: Guo, Jinjun, et al.
Publicado: (2020)

Macroscopic and Mesoscopic Deterioration Behaviors of Concrete under the Coupling Effect of Chlorine Salt Erosion and Freezing–Thawing Cycle
por: Chen, Shaojie, et al.
Publicado: (2021)

Deterioration characteristics of cement-improved loess under dry–wet and freeze–thaw cycles
por: Jiang, Ying-jun, et al.
Publicado: (2021)

Monitoring of Freeze-Thaw Cycles in Concrete Using Embedded Sensors and Ultrasonic Imaging
por: Ranz, Javier, et al.
Publicado: (2014)

Analysis of Acoustic Emission Signals Recorded during Freeze-Thaw Cycling of Concrete
por: Topolář, Libor, et al.
Publicado: (2021)

Influence of Varied Waste Ceramic Fillers on the Resistance of Concrete to Freeze–Thaw Cycles
por: Katzer, Jacek, et al.
Publicado: (2021)

The effects of soil freeze–thaw processes on water and salt migrations in the western Songnen Plain, China
por: Qin, Yan, et al.
Publicado: (2021)

Degradation Mechanism and Numerical Simulation of Pervious Concrete under Salt Freezing-Thawing Cycle
por: Xiang, Junzheng, et al.
Publicado: (2022)

Numerical Simulation of the Effect of Freeze-Thaw Cycles on the Axial Compression Strength of Rubber Concrete
por: Hao, Dingyi, et al.
Publicado: (2023)

Experimental Study on Mechanical Properties and Pore Structure Deterioration of Concrete under Freeze–Thaw Cycles
por: Zhang, Kai, et al.
Publicado: (2021)

Shear Bond Performance at Interface of Concrete-Filled Steel Tube after Freeze–Thaw Cycles
por: Xu, Bo, et al.
Publicado: (2022)

Experimental Study on Mechanical Properties of Basalt Fiber Concrete after Cryogenic Freeze−Thaw Cycles
por: Li, Yang, et al.
Publicado: (2022)

The Effects of Hybrid Steel/Basalt Fibers on the Durability of Concrete Pavement against Freeze–Thaw Cycles
por: Yu, Jianqiao, et al.
Publicado: (2023)

Effects of Thermal Conductive Materials on the Freeze-Thaw Resistance of Concrete
por: Woo, Byeong-Hun, et al.
Publicado: (2021)

Research on Fractal Characteristics and Energy Dissipation of Concrete Suffered Freeze-Thaw Cycle Action and Impact Loading
por: Li, Yan, et al.
Publicado: (2019)

The Influence of Freeze–Thaw Cycles and Corrosion on Reinforced Concrete and the Relationship between the Evolutions of the Microstructure and Mechanical Properties
por: Zhang, Shuhua, et al.
Publicado: (2022)

Degradation of Mechanical Properties of Graphene Oxide Concrete under Sulfate Attack and Freeze–Thaw Cycle Environment
por: Qian, Ji, et al.
Publicado: (2023)

Effectiveness of various types of coating materials applied in reinforced concrete exposed to freeze–thaw cycles and chlorides
por: Millán Ramírez, Ginneth Patricia, et al.
Publicado: (2023)

Influence of freeze-thawed cycles on pork quality
por: Tippala, Tiprawee, et al.
Publicado: (2021)

Performance of Plain Concrete and Cement Blocks with Cement Partially Replaced by Cement Kiln Dust
por: Alharthi, Yasir M., et al.
Publicado: (2021)

Effect of Freeze-Thaw Cycles on Triaxial Strength Property Damage to Cement Improved Aeolian Sand (CIAS)
por: Li, Jun, et al.
Publicado: (2019)

Effects of Freeze–Thaw Cycles on Water Migration, Microstructure and Protein Oxidation in Cuttlefish
por: Lv, Ying, et al.
Publicado: (2021)

Effects of Fiber and Surface Treatment on Airport Pavement Concrete against Freeze–Thawing and Salt Freezing
por: Xu, Lei, et al.
Publicado: (2022)

Nonlinear Resonance Vibration Assessment to Evaluate the Freezing and Thawing Resistance of Concrete
por: Kim, Jae Hong, et al.
Publicado: (2019)

Fractal Analysis of the Fracture Evolution of Freeze-Thaw Damage to Asphalt Concrete
por: Li, Jun, et al.
Publicado: (2019)

Advanced Evaluation of the Freeze–Thaw Damage of Concrete Based on the Fracture Tests
por: Kucharczyková, Barbara, et al.
Publicado: (2021)

Analytical Hysteretic Behavior of Square Concrete-Filled Steel Tube Pier Columns under Alternate Sulfate Corrosion and Freeze-Thaw Cycles
por: Zhang, Tong, et al.
Publicado: (2022)

Combined Freeze-Thaw and Chloride Attack Resistance of Concrete Made with Recycled Brick-Concrete Aggregate
por: Yu, Yao, et al.
Publicado: (2021)

Comprehensive Evaluation of the Sustainability of Waste Concrete towards Structural Concrete Application in Freeze-Thaw Environment
por: Wei, Da, et al.
Publicado: (2022)

Impact of Freeze–Thaw Cycles on the Long-Term Performance of Concrete Pavement and Related Improvement Measures: A Review
por: Luo, San, et al.
Publicado: (2022)

Sulfate Freeze–Thaw Resistance of Magnesium Potassium Phosphate Cement Mortar
por: Yang, Bin, et al.
Publicado: (2022)

Investigation on the Failure Behavior of Engineered Cementitious Composites under Freeze-Thaw Cycles
por: Zhong, Junfei, et al.
Publicado: (2019)

Cannot write session to /tmp/vufind_sessions/sess_pqfb1ee3ate549b9u6jg6sb1tb