Electrochemical Investigation of the Corrosion of Different Microstructural Phases of X65 Pipeline Steel under Saturated Carbon Dioxide Conditions

The aim of this research was to investigate the influence of metallurgy on the corrosion behaviour of separate weld zone (WZ) and parent plate (PP) regions of X65 pipeline steel in a solution of deionised water saturated with CO(2), at two different temperatures (55 °C and 80 °C) and at initial pH~4...

Descripción completa

Detalles Bibliográficos
Autores principales:	Yang, Yuanfeng, Joshi, Gaurav R., Akid, Robert
Formato:	Online Artículo Texto
Lenguaje:	English
Publicado:	MDPI 2015
Materias:	Article
Acceso en línea:	https://www.ncbi.nlm.nih.gov/pmc/articles/PMC5455576/ http://dx.doi.org/10.3390/ma8052635

Ejemplares similares

Correction: Electrochemical Investigation of the Corrosion of Different Microstructural Phases of X65 Pipeline Steel under Saturated Carbon Dioxide Conditions. Materials 2015, 8, 2635–2649
por: Yang, Yuanfeng, et al.
Publicado: (2015)

Effect of Pseudomonas aeruginosa on corrosion of X65 pipeline steel
por: Tang, Jianhua, et al.
Publicado: (2022)

Experimental Investigation on Corrosion Behavior of X80 Pipeline Steel under Carbon Dioxide Aqueous Conditions
por: Chen, Jukai, et al.
Publicado: (2022)

Investigation of erosion-corrosion failure of API X52 carbon steel pipeline
por: Abdu, Mahmoud T., et al.
Publicado: (2023)

Hydrogen Accumulation and Distribution in Pipeline Steel in Intensified Corrosion Conditions
por: Titov, Anatolii I., et al.
Publicado: (2019)

Recent Advances in Nondestructive Method and Assessment of Corrosion Undercoating in Carbon–Steel Pipelines
por: May, Zazilah, et al.
Publicado: (2022)

Microstructural, mechanical, and electrochemical analysis of carbon doped AISI carbon steels
por: Ishtiaq, Muhammad, et al.
Publicado: (2022)

Electrochemical corrosion behaviour of four low-carbon steels in saline soil
por: Qi, Gang, et al.
Publicado: (2022)

Electrochemical Study on the Macro-Cell Corrosion of Pipeline Steel Partially Covered by Different Kinds of Mineral Deposits
por: He, Limin, et al.
Publicado: (2023)

Structural Integrity of Steel Pipeline with Clusters of Corrosion Defects
por: Witek, Maciej
Publicado: (2021)

Enhancing Corrosion Resistance and Hardness Properties of Carbon Steel through Modification of Microstructure
por: Handoko, Wilson, et al.
Publicado: (2018)

Localized Corrosion Occurrence in Low-Carbon Steel Pipe Caused by Microstructural Inhomogeneity
por: Lee, Yun-Ho, et al.
Publicado: (2022)

Effect of H(2)S Corrosion on the Fracture Toughness of the X80 Pipeline Steel Welded Joint
por: Wang, Xueli, et al.
Publicado: (2022)

Corrosion of Carbon Steel in Artificial Geothermal Brine: Influence of Carbon Dioxide at 70 °C and 150 °C
por: Aristia, Gabriela, et al.
Publicado: (2019)

The Effect of Microstructural Changes on Mechanical and Electrochemical Corrosion Properties of Duplex Stainless Steel Aged for Short Periods
por: Silva, David D. S., et al.
Publicado: (2020)

The Evolution and Distribution of Microstructures in High-Energy Laser-Welded X100 Pipeline Steel
por: Wang, Gang, et al.
Publicado: (2019)

Corrosion Behavior of Alumina-Forming Austenitic Steel in Supercritical Carbon Dioxide Conditions: Effects of Nb Content and Temperature
por: Ma, Zhaodandan, et al.
Publicado: (2023)

The carbon footprint of steel corrosion
por: Iannuzzi, M., et al.
Publicado: (2022)

Investigation of the Microstructural and Corrosion Properties of Steels and Light Alloys
por: Pezzato, Luca, et al.
Publicado: (2023)

A Statistical Study on the Effect of Hydrostatic Pressure on Metastable Pitting Corrosion of X70 Pipeline Steel
por: Yang, Zixuan, et al.
Publicado: (2017)

Prediction of Corrosive Fatigue Life of Submarine Pipelines of API 5L X56 Steel Materials
por: Gao, Xudong, et al.
Publicado: (2019)

Corrosion behavior of X80 pipeline steel local defect pits under static liquid film
por: Tan, Zhuowei, et al.
Publicado: (2021)

Numerical Simulation of Damage Evolution and Electrode Deformation of X100 Pipeline Steel during Crevice Corrosion
por: Su, Wenxian, et al.
Publicado: (2022)

Inhibition Effect of Pseudomonas stutzeri on the Corrosion of X70 Pipeline Steel Caused by Sulfate-Reducing Bacteria
por: Qiu, Lina, et al.
Publicado: (2023)

The Corrosion Behavior of X100 Pipeline Steel in a Sodium Chloride Solution Containing Magnesium and Calcium
por: Yang, Xiaoning, et al.
Publicado: (2023)

Effect of Alcaligenes sp. on corrosion behavior of X65 steel in simulated offshore oilfield-produced water
por: Shi, Peiyu, et al.
Publicado: (2023)

A Comparative Study on the Electrochemical Corrosion Behavior of Iron and X-65 Steel in 4.0 wt % Sodium Chloride Solution after Different Exposure Intervals
por: Sherif, El-Sayed M.
Publicado: (2014)

Effect of Jet Impingement Velocity and Angle on CO(2) Erosion–Corrosion with and without Sand for API 5L-X65 Carbon Steel
por: Toor, Ihsan Ulhaq, et al.
Publicado: (2020)

Corrosion and hydrogen evolution rate control for X-65 carbon steel based on chitosan polymeric ionic liquids: experimental and quantum chemical studies
por: Elsaeed, S. M., et al.
Publicado: (2018)

Electrochemical Corrosion Behaviour of X70 Steel under the Action of Capillary Water in Saline Soils
por: Wei, Jianjian, et al.
Publicado: (2022)

Effect of Alternating Current and Sulfate-Reducing Bacteria on Corrosion of X80 Pipeline Steel in Soil-Extract Solution
por: Qing, Yongchang, et al.
Publicado: (2019)

Mechanical property degradation of X80 pipeline steel due to microbiologically influenced corrosion caused by Desulfovibrio vulgaris
por: Li, Zhong, et al.
Publicado: (2022)

Electrochemical and quantum chemical studies on the corrosion inhibition of 1037 carbon steel by different types of surfactants
por: El-Aziz S. Fouda, Abd, et al.
Publicado: (2022)

Analysis of the Physicochemical, Mechanical, and Electrochemical Parameters and Their Impact on the Internal and External SCC of Carbon Steel Pipelines
por: Quej-Ake, Luis Manuel, et al.
Publicado: (2020)

Effect of Annealing on Microstructure and Corrosion Behavior of Interstitial Free Steel
por: He, Qiongyao, et al.
Publicado: (2021)

Galvanic corrosion of duplex corrosion-resistant steel rebars under carbonated concrete conditions
por: Jiang, Jinyang, et al.
Publicado: (2018)

Quantitative Correlation between Thermal Cycling and the Microstructures of X100 Pipeline Steel Laser-Welded Joints
por: Wang, Gang, et al.
Publicado: (2019)

Microstructure, Mechanical Properties, and Corrosion Behavior of Ultra-Low Carbon Bainite Steel with Different Niobium Content
por: Zong, Yun, et al.
Publicado: (2021)

Electrochemical Noise Measurement to Assess Corrosion of Steel Reinforcement in Concrete
por: Mills, Douglas, et al.
Publicado: (2021)

Anticorrosion Investigation of New Diazene-Based Schiff Base Derivatives as Safe Corrosion Inhibitors for API X65 Steel Pipelines in Acidic Oilfield Formation Water: Synthesis, Experimental, and Computational Studies
por: A Altalhi, Amal
Publicado: (2023)

Cannot write session to /tmp/vufind_sessions/sess_hkiafdraivbgovhgar11jpekru