Corrosion Behavior of X80 Steel with Coupled Coating Defects under Alternating Current Interference in Alkaline Environment
The corrosion behavior of X80 steel in the presence of coupled coating defects was simulated and studied under the interference of alternating current (AC) in an alkaline environment. The results from electrochemical measurements showed that the electrode potential of the coating defect with the sma...
Autores principales: | Li, Zhong, Li, Caiyu, Qian, Hongchang, Li, Jun, Huang, Liang, Du, Cuiwei |
---|---|
Formato: | Online Artículo Texto |
Lenguaje: | English |
Publicado: |
MDPI
2017
|
Materias: | |
Acceso en línea: | https://www.ncbi.nlm.nih.gov/pmc/articles/PMC5551763/ https://www.ncbi.nlm.nih.gov/pubmed/28773078 http://dx.doi.org/10.3390/ma10070720 |
Ejemplares similares
-
Characteristic and Mechanistic Investigation of Stress-Assisted Microbiologically Influenced Corrosion of X80 Steel in Near-Neutral Solutions
por: Guo, Huihua, et al.
Publicado: (2022) -
Effect of Alternating Current on the Cathodic Protection and Interface Structure of X80 Steel
por: Wang, Huiru, et al.
Publicado: (2017) -
Effect of Al–Zn Alloy Coating on Corrosion Fatigue Behavior of X80 Riser Steel
por: Han, Zhongying, et al.
Publicado: (2019) -
Study on corrosion behavior of X80 steel under stripping coating by sulfate reducing bacteria
por: Cui, Yan-Yu, et al.
Publicado: (2021) -
Corrosion behavior of X80 pipeline steel local defect pits under static liquid film
por: Tan, Zhuowei, et al.
Publicado: (2021)