Effect of surface sealing on stain resistance of a nano-hybrid resin composite
PURPOSE: This study investigated the influence of sealant application on stain resistance of a nanohybrid resin composite compared to the efficacy of a bonding agent used as a surface sealant on prolonging color stability of the resin composite. MATERIALS AND METHODS: 28 disc-shaped materials were p...
Autores principales: | , , , , |
---|---|
Formato: | Online Artículo Texto |
Lenguaje: | English |
Publicado: |
Istanbul University Faculty of Dentisty
2015
|
Materias: | |
Acceso en línea: | https://www.ncbi.nlm.nih.gov/pmc/articles/PMC5573481/ https://www.ncbi.nlm.nih.gov/pubmed/28955532 http://dx.doi.org/10.17096/jiufd.24298 |
Sumario: | PURPOSE: This study investigated the influence of sealant application on stain resistance of a nanohybrid resin composite compared to the efficacy of a bonding agent used as a surface sealant on prolonging color stability of the resin composite. MATERIALS AND METHODS: 28 disc-shaped materials were prepared from a nano-hybrid resin composite Filtek Z550 and assigned to four groups: G1K: nonsealed; G2:Adper Single Bond; G3: Fortify ; G4: Biscover LV. After 24 h storage in distilled water at 37˚C, all specimens were subjected to thermocycling and immersed into coffee solution. Color measurements were performed using spectrophotometer (VITA Easyshade; Vident) according to CIEL*a*b* system. RESULTS: Color change values were significantly different among the groups in each evaluation period except for after thermocycling (p<0.05). For 7 days evaluation period, the difference between G3 and G4 group was statistically significant while G4 exhibited statistically significant differences (p<0.05 and p<0.0001 respectively) compared to control (G1) in 14 day whereas no significant difference was found between GI and GII in 28-day evaluation period. However, ΔE values of sealed specimens (GIII, GIV) differed significantly from non-sealed (GI) specimens after 28 days of immersion in coffee solution (p<0.05 and p<0.0001 respectively). CONCLUSION: It may be concluded that using a bonding agent as a surface sealant does not increase stain resistance of resin composites of the sealants evaluated. Biscover LV showed the highest efficacy to prolong color stability of the resin composite. |
---|