Pitting Initiation and Propagation of X70 Pipeline Steel Exposed to Chloride-Containing Environments

Inclusion-induced pitting initiation mechanisms in X70 steel were investigated by scanning electron microscopy, scanning Kelvin probe force microscopy (SKPFM), immersion and electrochemical polarization tests in chloride-containing ion solutions. There are three inclusion types in the X70 steel. Cor...

Descripción completa

Detalles Bibliográficos
Autores principales:	Yang, Zixuan, Kan, Bo, Li, Jinxu, Su, Yanjing, Qiao, Lijie, Volinsky, Alex A.
Formato:	Online Artículo Texto
Lenguaje:	English
Publicado:	MDPI 2017
Materias:	Article
Acceso en línea:	https://www.ncbi.nlm.nih.gov/pmc/articles/PMC5615730/ https://www.ncbi.nlm.nih.gov/pubmed/28902156 http://dx.doi.org/10.3390/ma10091076

Ejemplares similares

A Statistical Study on the Effect of Hydrostatic Pressure on Metastable Pitting Corrosion of X70 Pipeline Steel
por: Yang, Zixuan, et al.
Publicado: (2017)

Effects of Sodium Phosphate and Sodium Nitrite on the Pitting Corrosion Process of X70 Carbon Steel in Sodium Chloride Solution
por: Zhu, Yongyan, et al.
Publicado: (2020)

Combined Effect of Alternating Current Interference and Cathodic Protection on Pitting Corrosion and Stress Corrosion Cracking Behavior of X70 Pipeline Steel in Near-Neutral pH Environment
por: Wang, Liwei, et al.
Publicado: (2018)

Characterization of a Surface Hydrogen Charging Product Affecting the Mechanical Properties in 2205 Duplex Stainless Steel
por: Kan, Bo, et al.
Publicado: (2019)

The Corrosion Behavior of X100 Pipeline Steel in a Sodium Chloride Solution Containing Magnesium and Calcium
por: Yang, Xiaoning, et al.
Publicado: (2023)

Proton Irradiation Effects on Hardness and the Volta Potential of Welding 308L Duplex Stainless Steel
por: Jiang, Baolong, et al.
Publicado: (2018)

Corrosion behavior of X80 pipeline steel local defect pits under static liquid film
por: Tan, Zhuowei, et al.
Publicado: (2021)

Strengthening Effect of Nb on Ferrite Grain Boundary in X70 Pipeline Steel
por: Li, Zhongyi, et al.
Publicado: (2020)

A Review of Fatigue Crack Growth for Pipeline Steels Exposed to Hydrogen
por: Nanninga, N., et al.
Publicado: (2010)

Effect of Mo Content on Hydrogen Evolution Reaction of 1400 MPa-Grade High-Strength Bolt Steel
por: Xiong, Xilin, et al.
Publicado: (2023)

The Synergistic Inhibitions of Tungstate and Molybdate Anions on Pitting Corrosion Initiation for Q235 Carbon Steel in Chloride Solution
por: Yang, Huanggen, et al.
Publicado: (2022)

Assessment of the Corrosion of Steel Embedded in an Alkali-Activated Hybrid Concrete Exposed to Chlorides
por: Valencia-Saavedra, William, et al.
Publicado: (2022)

Study on micro crack propagation mechanism of ferrite–pearlite gas transmission pipeline steel with lamellar structure
por: Xu, Taolong, et al.
Publicado: (2022)

Corrosion Development of Carbon Steel Grids and Shear Connectors in Cracked Composite Beams Exposed to Wet–Dry Cycles in Chloride Environment
por: Xue, Wen, et al.
Publicado: (2018)

Inhibition Effect of Pseudomonas stutzeri on the Corrosion of X70 Pipeline Steel Caused by Sulfate-Reducing Bacteria
por: Qiu, Lina, et al.
Publicado: (2023)

Corrosion of Steel Rebars in Anoxic Environments. Part II: Pit Growth Rate and Mechanical Strength
por: Garcia, Elena, et al.
Publicado: (2021)

Pitting Corrosion Behaviour of New Corrosion-Resistant Reinforcement Bars in Chloride-Containing Concrete Pore Solution
por: Jiang, Jin-yang, et al.
Publicado: (2017)

Development and optimization of trivalent chromium electrodeposit on 304L stainless steel to improve corrosion resistance in chloride-containing environment
por: Okonkwo, Bright O., et al.
Publicado: (2023)

Effect of Relative Humidity on Mechanical Degradation of Medium Mn Steels
por: Liu, Qingyang, et al.
Publicado: (2020)

Pipeline steels for sour service
por: Shabalov, Ivan, et al.
Publicado: (2018)

Stress Corrosion Cracking of an Austenitic Stainless Steel in Nitrite-Containing Chloride Solutions
por: Singh Raman, R. K., et al.
Publicado: (2014)

Monitoring the Corrosion of Steel in Concrete Exposed to a Marine Environment
por: Gartner, Nina, et al.
Publicado: (2020)

Effects of chloride ions on corrosion of ductile iron and carbon steel in soil environments
por: Song, Yarong, et al.
Publicado: (2017)

Research on the Corrosion Behavior of Q235 Pipeline Steel in an Atmospheric Environment through Experiment
por: Cai, Shuo, et al.
Publicado: (2022)

Modeling of Hydrogen-Charged Notched Tensile Tests of an X70 Pipeline Steel with a Hydrogen-Informed Gurson Model
por: Depraetere, Robin, et al.
Publicado: (2023)

Assessment of Operational Degradation of Pipeline Steels
por: Nykyforchyn, Hryhoriy, et al.
Publicado: (2021)

Mechanical Performance of Steel Fibre Reinforced Concrete Exposed to Wet–Dry Cycles of Chlorides and Carbon Dioxide
por: Marcos-Meson, Victor, et al.
Publicado: (2021)

The Corrosion Susceptibility of 304L Stainless Steel Exposed to Crevice Environments
por: Tsai, Kun-Chao, et al.
Publicado: (2022)

Determination of Iron Valence States Around Pits and the Influence of Fe(3+) on the Pitting Corrosion of 304 Stainless Steel
por: Zhang, Hao, et al.
Publicado: (2020)

Evaluation of the Influence of the Combination of pH, Chloride, and Sulfate on the Corrosion Behavior of Pipeline Steel in Soil Using Response Surface Methodology
por: Chung, Nguyen Thuy, et al.
Publicado: (2021)

Efficiency of generic and proprietary inhibitors in mitigating Corrosion of Carbon Steel in Chloride-Sulfate Environments
por: Al-Sodani, Khaled A. Alawi, et al.
Publicado: (2018)

Interacting Effects Induced by Two Neighboring Pits Considering Relative Position Parameters and Pit Depth
por: Huang, Yongfang, et al.
Publicado: (2017)

Corrosion Resistance of Calcium Aluminate Cement Concrete Exposed to a Chloride Environment
por: Ann, Ki Yong, et al.
Publicado: (2014)

Prediction of Crack Width in RC Piles Exposed to Local Corrosion in Chloride Environment
por: Shao, Wei, et al.
Publicado: (2023)

Pits in Metals Caused by Collision With Liquid Drops and Rigid Steel Spheres
por: Engel, Olive G.
Publicado: (1960)

Microstructure and Pitting Corrosion of Austenite Stainless Steel after Crack Arrest
por: Zhang, Zhuwu, et al.
Publicado: (2019)

Construction of Complex Structures Containing Micro-Pits and Nano-Pits on the Surface of Titanium for Cytocompatibility Improvement
por: Wang, Guisen, et al.
Publicado: (2019)

Composition of Corroded Reinforcing Steel Surface in Solutions Simulating the Electrolytic Environments in the Micropores of Concrete in the Propagation Period
por: Saura, Pascual, et al.
Publicado: (2022)

Atomic-scale decoration for improving the pitting corrosion resistance of austenitic stainless steels
por: Zhou, Y. T., et al.
Publicado: (2014)

Influence of Ethanol on Pitting Corrosion Behavior of Stainless Steel for Bioethanol Fermentation Tanks
por: Wan, Yiting, et al.
Publicado: (2020)

Cannot write session to /tmp/vufind_sessions/sess_jfcemj416v5blq1fb2uqdptt0m