Dynamic Recrystallization of the Constituent γ Phase and Mechanical Properties of Ti-43Al-9V-0.2Y Alloy Sheet
A crack-free Ti-43Al-9V-0.2Y alloy sheet was successfully fabricated via hot-pack rolling at 1200 °C. After hot-rolling, the β/γ lamellar microstructure of the as-forged TiAl alloy was completely converted into a homogeneous duplex microstructure with an average γ grain size of 10.5 μm. The dynamic...
Autores principales: | Zhang, Yu, Wang, Xiaopeng, Kong, Fantao, Chen, Yuyong |
---|---|
Formato: | Online Artículo Texto |
Lenguaje: | English |
Publicado: |
MDPI
2017
|
Materias: | |
Acceso en línea: | https://www.ncbi.nlm.nih.gov/pmc/articles/PMC5615743/ https://www.ncbi.nlm.nih.gov/pubmed/28914797 http://dx.doi.org/10.3390/ma10091089 |
Ejemplares similares
-
Microstructure Evolution and Mechanical Properties of PM-Ti43Al9V0.3Y Alloy
por: Zhang, Dongdong, et al.
Publicado: (2020) -
Hot Deformation Behavior and Microstructural Evolution of PM Ti43Al9V0.3Y with Fine Equiaxed γ and B2 Grain Microstructure
por: Zhang, Dongdong, et al.
Publicado: (2020) -
Prediction of Strength and Ductility in Partially Recrystallized CoCrFeNiTi(0.2) High-Entropy Alloy
por: Zhang, Hanwen, et al.
Publicado: (2019) -
The Effects of a Trace Amount of Manganese and the Homogenization on the Recrystallization of Al–7Mg–0.15Ti Alloys
por: Chiu, Yang-Chun, et al.
Publicado: (2020) -
Effect of transition metal alloying elements on the deformation of Ti-44Al-8Nb-0.2B-0.2Y alloys
por: Zhang, Laiqi, et al.
Publicado: (2018)