A Statistical Study on the Effect of Hydrostatic Pressure on Metastable Pitting Corrosion of X70 Pipeline Steel
Hydrostatic pressure effects on pitting initiation and propagation in X70 steel are investigated by evaluating metastable pitting probability using electrochemical methods and immersion corrosion tests in containing chlorine ion solution. Potentiodynamic tests indicated that hydrostatic pressure can...
Autores principales: | Yang, Zixuan, Kan, Bo, Li, Jinxu, Su, Yanjing, Qiao, Lijie, Volinsky, Alex A. |
---|---|
Formato: | Online Artículo Texto |
Lenguaje: | English |
Publicado: |
MDPI
2017
|
Materias: | |
Acceso en línea: | https://www.ncbi.nlm.nih.gov/pmc/articles/PMC5706254/ https://www.ncbi.nlm.nih.gov/pubmed/29135912 http://dx.doi.org/10.3390/ma10111307 |
Ejemplares similares
-
Pitting Initiation and Propagation of X70 Pipeline Steel Exposed to Chloride-Containing Environments
por: Yang, Zixuan, et al.
Publicado: (2017) -
Coupling Effect
of Hydrostatic Pressure and Erosion
on Corrosion Behavior of X70 Steel in Simulated Seawater
por: Ren, PengWei, et al.
Publicado: (2022) -
Corrosion behavior of X80 pipeline steel local defect pits under static liquid film
por: Tan, Zhuowei, et al.
Publicado: (2021) -
Combined Effect of Alternating Current Interference and Cathodic Protection on Pitting Corrosion and Stress Corrosion Cracking Behavior of X70 Pipeline Steel in Near-Neutral pH Environment
por: Wang, Liwei, et al.
Publicado: (2018) -
Inhibition Effect of Pseudomonas stutzeri on the Corrosion of X70 Pipeline Steel Caused by Sulfate-Reducing Bacteria
por: Qiu, Lina, et al.
Publicado: (2023)