Fracture resistance of posterior teeth restored with high-viscosity bulk-fill resin composites in comparison to the incremental placement technique

AIM: Comparative evaluation of the fracture resistance of maxillary premolar teeth restored with two high-viscosity bulk-fill composites and incrementally placed composite. MATERIALS AND METHODS: Seventy-five freshly extracted maxillary premolar teeth were selected. Fifteen specimens served as positive control (Group 1). Mesio-occluso-distal cavity preparation was prepared on the rest of the specimens. These specimens were further divided into four groups: unrestored teeth (Group 2), teeth restored with incrementally placed nanocomposite (Group 3), teeth restored with high-viscosity bulk-fill giomer (Group 4), and teeth restored with high-viscosity bulk-fill nanocomposite (Group 5). The specimens were then subjected to compressive axial load using Instron universal testing machine. Data were analyzed using data were analyzed using Statistical package for social sciences software (SPSS v 20.0, IBM Corp.). RESULTS: The positive control group exhibited highest fracture resistance (1104.70 ± 122.2 N). There was no statistically significant difference seen in between the incrementally placed nanocomposite and high-viscosity nanocomposite (P > 0.05). The fracture resistance values displayed by the high-viscosity bulk-fill giomer were found to be statistically lower than the other two groups. CONCLUSION: High-viscosity bulk-fill nanocomposite may substitute incrementally placed nanocomposite with respect to fracture resistance.