Comparison of the effectiveness of Tokuyama and GC II metal primer on the bond strength of acrylic resins to Ti-6Al-7Nb

STATEMENT OF PROBLEM: Because of the toxicity of vanadium in Ti-6Al-4V alloy, next generation of titanium alloys is proposed to focus on niobium-containing alloy, but for clinical applications, it is crucial for this alloy to bond with acrylic resins with or without the use of primers. However, literature was lacking about the effect of primers on bonding of autopolymerizing resins to Ti-6Al-7Nb. OBJECTIVES: To evaluate the effect of different metal primers on the shear bond strength of acrylic resin to Ti-6Al-7Nb. MATERIALS AND METHODS: A total of 30 dis-shaped wax patterns (10 mm in diameter and 2 mm thickness) were prepared and casted using Ti-6Al-7Nb. After casting, the disk surfaces were finished with abrasive paper under water. Specimens were equally divided into three groups on the basis of the use of primer: metal primer (GC II metal primer) (Group 1), Universal Tokuyama primer (Group 2), no primer (Group 3). Tape of 50 μm thickness was applied on each of the specimens. Then, self-cure acrylic resin was mixed and applied on the center part of the tape, on which Bernouilles tube was placed. The tensile bond strength was measured with a universal testing machine. The data were obtained for all the specimens and analyzed using Statistical Package for Social Sciences version 17.0 at a statistically significance level of <0.05. RESULTS: Mean tensile force was maximum for Group 2 (28.58 ± 39.40 N) and minimum for control Group 3 (6.24 ± 10.97 N), thereby showing a significant inter-group difference (P < 0.001). On applying post hoc test (Tukey HSD), both the Group 1 and Group 2 showed a statistically significant difference as compared to control Group 3; however, the difference between two experimental groups was not statistically significant (P > 0.05). CONCLUSIONS: Tokuyama primer and GC II metal primer had a significant effect on improving the bond strength between autopolymerizing denture base resin and Ti-6Al-7Nb.