Microstructure and Tensile Properties of Friction Stir Processed Mg–Sn–Zn Alloy
In this study, as-cast Mg–6Sn–2Zn (wt.%) alloy was subjected to friction stir processing (FSP) and the microstructure and tensile properties of FSP Mg–6Sn–2Zn samples were investigated. It was found that, in the stir zone (SZ) of FSP Mg–6Sn–2Zn samples, α-Mg grains were significantly refined via dyn...
Autores principales: | , , , , |
---|---|
Formato: | Online Artículo Texto |
Lenguaje: | English |
Publicado: |
MDPI
2018
|
Materias: | |
Acceso en línea: | https://www.ncbi.nlm.nih.gov/pmc/articles/PMC5951529/ https://www.ncbi.nlm.nih.gov/pubmed/29690590 http://dx.doi.org/10.3390/ma11040645 |
Sumario: | In this study, as-cast Mg–6Sn–2Zn (wt.%) alloy was subjected to friction stir processing (FSP) and the microstructure and tensile properties of FSP Mg–6Sn–2Zn samples were investigated. It was found that, in the stir zone (SZ) of FSP Mg–6Sn–2Zn samples, α-Mg grains were significantly refined via dynamic recrystallization (DRX) and the Mg(2)Sn phase was broken and partially dissolved. The microstructure in SZ was nonuniform and DRXed grains in the SZ-up regions were coarser than those in the SZ-down regions. Coarse broken Mg(2)Sn particles were observed in the SZ-up regions, while only fine Mg(2)Sn particles were observed in the SZ-down regions. Strong {0001} basal texture developed in the SZ regions of Mg–6Sn–2Zn samples after FSP. The increase of travel speed had little effect on the texture of different SZ regions. The ductility of FSP Mg–6Sn–2Zn samples was obviously improved, while the improvement in strength was negligible when compared to the as-cast sample. The tensile properties of FSP Mg–6Sn–2Zn samples were influenced by grain refinement, texture modification, and the breaking up and dissolution of the Mg(2)Sn phase. |
---|