Uniform cobalt nanoparticles embedded in hexagonal mesoporous nanoplates as a magnetically separable, recyclable adsorbent

Novel hexagonal nanoplates (NPLs) comprised of mesoporous carbon containing imbedded magnetic Co nanoparticles (CoAl(2)O(4) phase) are prepared through direct carbonization of polydopamine (PDA)-coated CoAl layered double hydroxide (LDH). A uniform PDA coating initially covers the surface of LDH by dopamine self-polymerization under mild conditions. Well-dispersed Co nanoparticles are formed in the NPLs by the partial reduction of cobalt from Co(2+) to Co(0) with surface carbon during the heat treatment process. The surface morphology and specific surface area of the as-prepared NPLs can be tailored by adjusting the initial dopamine concentration and carbonization temperature. The mesoporous NPLs exhibit excellent sorption of rhodamine B (RhB) dye and fast magnetic separation in aqueous solution. Over 95% of RhB can be adsorbed within 2 min and the adsorption reaches equilibrium after about 30 min. The maximum adsorption capacity approaches 172.41 mg/g. After regeneration, this adsorbent can be recycled easily by magnetic separation and still possess good adsorption capacity for RhB removal, even after five cycles.