Symmetry broken spin reorientation transition in epitaxial MgO/Fe/MgO layers with competing anisotropies

The observation of perpendicular magnetic anisotropy (PMA) at MgO/Fe interfaces boosted the development of spintronic devices based on ultrathin ferromagnetic layers. Yet, magnetization reversal in the standard magnetic tunnel junctions (MTJs) with competing PMA and in-plane anisotropies remains unclear. Here we report on the field induced nonvolatile broken symmetry magnetization reorientation transition from the in-plane to the perpendicular (out of plane) state at temperatures below 50 K. The samples were 10 nm thick Fe in MgO/Fe(100)/MgO as stacking components of V/MgO/Fe/MgO/Fe/Co double barrier MTJs with an area of 20 × 20 μm(2). Micromagnetic simulations with PMA and different second order anisotropies at the opposite Fe/MgO interfaces qualitatively reproduce the observed broken symmetry spin reorientation transition. Our findings open the possibilities to develop multistate epitaxial spintronics based on competing magnetic anisotropies.