Type of Primary Nb(5)Si(3) and Precipitation of Nb(ss) in αNb(5)Si(3) in a Nb-8.3Ti-21.1Si-5.4Mo-4W-0.7Hf (at.%) Near Eutectic Nb-Silicide-Based Alloy

The Nb-silicide-based alloy of near eutectic composition (at.%) Nb-21.1Si-8.3Ti-5.4Mo-4W-0.7Hf (alloy CM1) was studied in the cast and heat-treated (1500 °C/100 h) conditions. The alloy was produced in the form of buttons and bars using three different methods, namely arc-melting, arc-melting and su...

Descripción completa

Detalles Bibliográficos
Autores principales: McCaughey, Conor, Tsakiropoulos, Panos
Formato: Online Artículo Texto
Lenguaje:English
Publicado: MDPI 2018
Materias:
Acceso en línea:https://www.ncbi.nlm.nih.gov/pmc/articles/PMC6024954/
https://www.ncbi.nlm.nih.gov/pubmed/29880762
http://dx.doi.org/10.3390/ma11060967
_version_ 1783336172358991872
author McCaughey, Conor
Tsakiropoulos, Panos
author_facet McCaughey, Conor
Tsakiropoulos, Panos
author_sort McCaughey, Conor
collection PubMed
description The Nb-silicide-based alloy of near eutectic composition (at.%) Nb-21.1Si-8.3Ti-5.4Mo-4W-0.7Hf (alloy CM1) was studied in the cast and heat-treated (1500 °C/100 h) conditions. The alloy was produced in the form of buttons and bars using three different methods, namely arc-melting, arc-melting and suction casting, and optical floating zone (OFZ) melting. In the former two cases the alloy solidified in water-cooled copper crucibles. Buttons and suction-cast bars of different size, respectively of 10 g and 600 g weight and 6 mm and 8 mm diameter, were produced. The OFZ bars were grown at three different growth rates of 12, 60 and 150 mm/h. It was confirmed that the type of Nb(5)Si(3) formed in the cast microstructures depended on the solidification conditions. The primary phase in the alloy CM1 was the βNb(5)Si(3). The transformation of βNb(5)Si(3) to αNb(5)Si(3) had occurred in the as cast large size button and the OFZ bars grown at the three different growth rates, and after the heat treatment of the small size button and the suction-cast bars of the alloy. This transformation was accompanied by subgrain formation in Nb(5)Si(3) and the precipitation of Nb(ss) in the large size as cast button and only by the precipitation of Nb(ss) in the cast OFZ bars. Subgrains and precipitation of Nb(ss) in αNb(5)Si(3) was observed in the small size button and suction-cast bars after the heat treatment. Subgrains formed in αNb(5)Si(3) after the heat treatment of the OFZ bars. The partitioning of solutes and in particular of Mo and Ti was key to this phase transformation. Subgrain formation was not necessary for precipitation of Nb(ss) in αNb(5)Si(3), but the partitioning of solutes was essential for this precipitation.
format Online
Article
Text
id pubmed-6024954
institution National Center for Biotechnology Information
language English
publishDate 2018
publisher MDPI
record_format MEDLINE/PubMed
spelling pubmed-60249542018-07-09 Type of Primary Nb(5)Si(3) and Precipitation of Nb(ss) in αNb(5)Si(3) in a Nb-8.3Ti-21.1Si-5.4Mo-4W-0.7Hf (at.%) Near Eutectic Nb-Silicide-Based Alloy McCaughey, Conor Tsakiropoulos, Panos Materials (Basel) Article The Nb-silicide-based alloy of near eutectic composition (at.%) Nb-21.1Si-8.3Ti-5.4Mo-4W-0.7Hf (alloy CM1) was studied in the cast and heat-treated (1500 °C/100 h) conditions. The alloy was produced in the form of buttons and bars using three different methods, namely arc-melting, arc-melting and suction casting, and optical floating zone (OFZ) melting. In the former two cases the alloy solidified in water-cooled copper crucibles. Buttons and suction-cast bars of different size, respectively of 10 g and 600 g weight and 6 mm and 8 mm diameter, were produced. The OFZ bars were grown at three different growth rates of 12, 60 and 150 mm/h. It was confirmed that the type of Nb(5)Si(3) formed in the cast microstructures depended on the solidification conditions. The primary phase in the alloy CM1 was the βNb(5)Si(3). The transformation of βNb(5)Si(3) to αNb(5)Si(3) had occurred in the as cast large size button and the OFZ bars grown at the three different growth rates, and after the heat treatment of the small size button and the suction-cast bars of the alloy. This transformation was accompanied by subgrain formation in Nb(5)Si(3) and the precipitation of Nb(ss) in the large size as cast button and only by the precipitation of Nb(ss) in the cast OFZ bars. Subgrains and precipitation of Nb(ss) in αNb(5)Si(3) was observed in the small size button and suction-cast bars after the heat treatment. Subgrains formed in αNb(5)Si(3) after the heat treatment of the OFZ bars. The partitioning of solutes and in particular of Mo and Ti was key to this phase transformation. Subgrain formation was not necessary for precipitation of Nb(ss) in αNb(5)Si(3), but the partitioning of solutes was essential for this precipitation. MDPI 2018-06-07 /pmc/articles/PMC6024954/ /pubmed/29880762 http://dx.doi.org/10.3390/ma11060967 Text en © 2018 by the authors. Licensee MDPI, Basel, Switzerland. This article is an open access article distributed under the terms and conditions of the Creative Commons Attribution (CC BY) license (http://creativecommons.org/licenses/by/4.0/).
spellingShingle Article
McCaughey, Conor
Tsakiropoulos, Panos
Type of Primary Nb(5)Si(3) and Precipitation of Nb(ss) in αNb(5)Si(3) in a Nb-8.3Ti-21.1Si-5.4Mo-4W-0.7Hf (at.%) Near Eutectic Nb-Silicide-Based Alloy
title Type of Primary Nb(5)Si(3) and Precipitation of Nb(ss) in αNb(5)Si(3) in a Nb-8.3Ti-21.1Si-5.4Mo-4W-0.7Hf (at.%) Near Eutectic Nb-Silicide-Based Alloy
title_full Type of Primary Nb(5)Si(3) and Precipitation of Nb(ss) in αNb(5)Si(3) in a Nb-8.3Ti-21.1Si-5.4Mo-4W-0.7Hf (at.%) Near Eutectic Nb-Silicide-Based Alloy
title_fullStr Type of Primary Nb(5)Si(3) and Precipitation of Nb(ss) in αNb(5)Si(3) in a Nb-8.3Ti-21.1Si-5.4Mo-4W-0.7Hf (at.%) Near Eutectic Nb-Silicide-Based Alloy
title_full_unstemmed Type of Primary Nb(5)Si(3) and Precipitation of Nb(ss) in αNb(5)Si(3) in a Nb-8.3Ti-21.1Si-5.4Mo-4W-0.7Hf (at.%) Near Eutectic Nb-Silicide-Based Alloy
title_short Type of Primary Nb(5)Si(3) and Precipitation of Nb(ss) in αNb(5)Si(3) in a Nb-8.3Ti-21.1Si-5.4Mo-4W-0.7Hf (at.%) Near Eutectic Nb-Silicide-Based Alloy
title_sort type of primary nb(5)si(3) and precipitation of nb(ss) in αnb(5)si(3) in a nb-8.3ti-21.1si-5.4mo-4w-0.7hf (at.%) near eutectic nb-silicide-based alloy
topic Article
url https://www.ncbi.nlm.nih.gov/pmc/articles/PMC6024954/
https://www.ncbi.nlm.nih.gov/pubmed/29880762
http://dx.doi.org/10.3390/ma11060967
work_keys_str_mv AT mccaugheyconor typeofprimarynb5si3andprecipitationofnbssinanb5si3inanb83ti211si54mo4w07hfatneareutecticnbsilicidebasedalloy
AT tsakiropoulospanos typeofprimarynb5si3andprecipitationofnbssinanb5si3inanb83ti211si54mo4w07hfatneareutecticnbsilicidebasedalloy