Pore Structure Characterization of Sodium Hydroxide Activated Slag Using Mercury Intrusion Porosimetry, Nitrogen Adsorption, and Image Analysis

The pore structure of alkali-activated slag has a significant influence on its performance. However, the literature shows insufficient studies regarding the suitability of different techniques for characterizing the pore structure and the influences of Na(2)O and curing age on pore structure development. In pursuit of a better understanding, the pore structure of sodium hydroxide activated slag paste was characterized by multiple techniques, e.g., mercury intrusion porosimetry (MIP), nitrogen (N(2)) adsorption, and scanning electron microscopy (SEM) image analysis. The sodium hydroxide activated slag pastes were prepared with three different contents of Na(2)O (Na(2)O/slag = 4, 6, and 8%) and cured for different times up to 360 days. The microstructure observation reveals that outer C–(N–)A–S–H and inner C–(N–)A–S–H grow successively around the reacting slag grains, along with crystalline reaction products which are formed in the empty coarse pore space. The increase of Na(2)O content and curing age lead to a finer pore structure. The MIP measurements show that the total porosity drops about 70% within the first day, and that one peak at most, corresponding to gel pores, was identified in the differential curves of all the investigated samples from 1 to 360 days. On the contrary, only one peak, corresponding to capillary pores, was identified by SEM-image analysis. The differential curves derived from N(2) adsorption generally reveal two peaks, and the trend that the pore diameters of those two peaks vary with curing age depends on the content of Na(2)O. Compared to Portland cement, sodium hydroxide activated slag has a higher pore space filling capacity (χ, V(products)/V(slag-reacted)), while the capacity decreases with increasing Na(2)O content and curing age.